{"title":"Enhanced dielectric properties of alumina ceramic substrate for microwave application","authors":"Dai Zhou, Pang Xueman, Cheng Kai, W. Ziliang","doi":"10.1109/RFIT.2012.6401627","DOIUrl":null,"url":null,"abstract":"Alumina ceramic with enhanced dielectric property was reported in this paper, which indicates its microwave application. Commercial A1203 powder and sintering aids including MgO were utilized to fabricate alumina ceramic substrate. Liquid deposit was introduced to wrap the surface of A1203 powder with MgO additives uniformly. The prepared composite powder was shaped by tape casting and sintered by two-step sintering to ensure density and suitable microstructure. It is shown that MgO addition restrains gain growing and decreases porosity in scanning electron micrograph. MgA1204 spinel, formed by MgO was detected by XRD. The dielectric loss of the alumina ceramic substrate is 6.84 × 10-4.","PeriodicalId":187550,"journal":{"name":"2012 IEEE International Symposium on Radio-Frequency Integration Technology (RFIT)","volume":"69 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2012-11-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"2","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"2012 IEEE International Symposium on Radio-Frequency Integration Technology (RFIT)","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1109/RFIT.2012.6401627","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 2
Abstract
Alumina ceramic with enhanced dielectric property was reported in this paper, which indicates its microwave application. Commercial A1203 powder and sintering aids including MgO were utilized to fabricate alumina ceramic substrate. Liquid deposit was introduced to wrap the surface of A1203 powder with MgO additives uniformly. The prepared composite powder was shaped by tape casting and sintered by two-step sintering to ensure density and suitable microstructure. It is shown that MgO addition restrains gain growing and decreases porosity in scanning electron micrograph. MgA1204 spinel, formed by MgO was detected by XRD. The dielectric loss of the alumina ceramic substrate is 6.84 × 10-4.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们