{"title":"Use of Electron Fractography to Diagnose Cracking in an AISI 4340 Nose Landing Gear Cylinder","authors":"J. A. Scott","doi":"10.31399/asm.fach.aero.c9001538","DOIUrl":null,"url":null,"abstract":"\n Examination of a cracked nose landing gear cylinder made of AISI 4340 Cr-Mo-Ni alloy steel proved that the part started to fail on the inside diam. When the nucleus of the stress-corrosion crack was studied in detail, iron oxide was found on the fracture surface. A 6500x micrograph revealed this area also displayed an intergranular texture. One of a group of small grinding cracks on the ID of the cylinder nucleated the failure. Other evidence indicated the cracks developed when the cylinder was ground during overhaul.","PeriodicalId":326464,"journal":{"name":"ASM Failure Analysis Case Histories: Air and Spacecraft","volume":"25 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2019-06-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"ASM Failure Analysis Case Histories: Air and Spacecraft","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.31399/asm.fach.aero.c9001538","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
Examination of a cracked nose landing gear cylinder made of AISI 4340 Cr-Mo-Ni alloy steel proved that the part started to fail on the inside diam. When the nucleus of the stress-corrosion crack was studied in detail, iron oxide was found on the fracture surface. A 6500x micrograph revealed this area also displayed an intergranular texture. One of a group of small grinding cracks on the ID of the cylinder nucleated the failure. Other evidence indicated the cracks developed when the cylinder was ground during overhaul.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们