{"title":"Electrical resistivity of heat-treated charcoal","authors":"R.D. Cromarty, S. Bharat, D. Odendaal","doi":"10.17159/2411-9717/2477/2023","DOIUrl":null,"url":null,"abstract":"The aim of this investigation was to determine the effect of high-temperature heat treatment on the electrical resistivity of charcoal. Samples of two different wood types (eucalyptus and black wattle) were pyrolised in a retort at a temperature of 700°C and the resulting charcoals heat-treated in an induction furnace at temperatures from 800°C to 1800°C and residence times from 60 to 120 minutes. After cooling, the resistivities of the samples were measured at room temperature using the four-point probe technique. It was found that as the heat treatment temperature increased the electrical resistivity of the charcoal decreased, approaching an asymptotic value at higher temperatures. Longer residence times decreased the resistivity, but this effect was not pronounced.","PeriodicalId":49025,"journal":{"name":"Journal of the Southern African Institute of Mining and Metallurgy","volume":"69 11-12","pages":""},"PeriodicalIF":0.7000,"publicationDate":"2023-11-15","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of the Southern African Institute of Mining and Metallurgy","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.17159/2411-9717/2477/2023","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"METALLURGY & METALLURGICAL ENGINEERING","Score":null,"Total":0}
引用次数: 0
Abstract
The aim of this investigation was to determine the effect of high-temperature heat treatment on the electrical resistivity of charcoal. Samples of two different wood types (eucalyptus and black wattle) were pyrolised in a retort at a temperature of 700°C and the resulting charcoals heat-treated in an induction furnace at temperatures from 800°C to 1800°C and residence times from 60 to 120 minutes. After cooling, the resistivities of the samples were measured at room temperature using the four-point probe technique. It was found that as the heat treatment temperature increased the electrical resistivity of the charcoal decreased, approaching an asymptotic value at higher temperatures. Longer residence times decreased the resistivity, but this effect was not pronounced.
期刊介绍：
The Journal serves as a medium for the publication of high quality scientific papers. This requires that the papers that are submitted for publication are properly and fairly refereed and edited. This process will maintain the high quality of the presentation of the paper and ensure that the technical content is in line with the accepted norms of scientific integrity.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们