Fast Synthesis of Fine Boron Carbide Powders Using Electromagnetic Induction Synthesis Method

Abstract

Boron carbide (B4C) powders with defined stoichiometry, high crystallinity, minimal impurity content, and a fine particle size are imperative for realizing the exceptional properties of this compound in advanced high-technology applications. Nevertheless, achieving the desired stoichiometry and particle size using traditional synthesis methods, which rely on prolonged high-temperature processes, can be challenging. The primary objective of this study is to synthesize fine B4C powders characterized by high crystallinity and a sub-micron particle size, employing a fast and energy-efficient method. B4C powders are synthesized from elemental boron and carbon in a high-frequency induction heating furnace using the electromagnetic induction synthesis (EMIS) method. The rapid heating rate achieved through contactless heating promotes the ignition and propagation of the exothermic chemical reaction between boron and carbon. Additionally, electromagnetic effects accelerate atomic diffusion, allowing the reaction to be completed in an exceptionally short timeframe. The grain size and crystallinity of B4C can be finely tuned by adjusting various process parameters, including the post-ignition holding temperature and the duration of heating. As a result, fine B4C powders can be synthesized in under 10 min. Moreover, these synthesized B4C powders exhibit oxidation onset temperatures higher than 500 °C when exposed to air.