Different Lattice Distortion Effects on the Tensile Properties of Ni-W Dilute Solutions and CrFeNi and CoCrFeMnNi Concentrated Solutions

Kuan-Hao Lin, C. Tseng, Chu-Chun Chueh, Shou-Yi Chang, Y. Lo, Wang, Su-Jien Lin, J. Yeh
{"title":"Different Lattice Distortion Effects on the Tensile Properties of Ni-W Dilute Solutions and CrFeNi and CoCrFeMnNi Concentrated Solutions","authors":"Kuan-Hao Lin, C. Tseng, Chu-Chun Chueh, Shou-Yi Chang, Y. Lo, Wang, Su-Jien Lin, J. Yeh","doi":"10.2139/ssrn.3834123","DOIUrl":null,"url":null,"abstract":"The lattice distortion from a solute is mainly due to atomic size and chemical bonding differences with neighboring atoms. The lattice distortion effects in conventional alloys and high-entropy alloys are known to be different but lack of clarification. In this study, FCC-structured dilute solid solutions of Ni, Ni–2at.%W, and Ni–4at.%W and concentrated solutions of equiatomic CrFeNi and CoCrFeMnNi metals were designed to compare their tensile properties. The lattice distortion of both W-containing alloys was only around the large and strong W atoms but that of the two concentrated solutions with similar inter-element atomic size and shear modulus prevailed at all lattice sites. Results showed that the trends in both types of lattice distortion were significantly different on tensile properties. The combination with strength and ductility from high concentration of distorted lattice points was superior over that from low concentration ones even the latter had larger nominal atomic size difference and shear modulus difference. The evolution mechanisms on different mechanical properties from dilute alloys to concentrated alloys were elucidated and clarified under the large contrast of lattice distortion. The universal solid solution strengthening mechanism had been established.","PeriodicalId":18255,"journal":{"name":"MatSciRN: Process & Device Modeling (Topic)","volume":"4 1","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2021-04-26","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"13","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"MatSciRN: Process & Device Modeling (Topic)","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.2139/ssrn.3834123","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 13

Abstract

The lattice distortion from a solute is mainly due to atomic size and chemical bonding differences with neighboring atoms. The lattice distortion effects in conventional alloys and high-entropy alloys are known to be different but lack of clarification. In this study, FCC-structured dilute solid solutions of Ni, Ni–2at.%W, and Ni–4at.%W and concentrated solutions of equiatomic CrFeNi and CoCrFeMnNi metals were designed to compare their tensile properties. The lattice distortion of both W-containing alloys was only around the large and strong W atoms but that of the two concentrated solutions with similar inter-element atomic size and shear modulus prevailed at all lattice sites. Results showed that the trends in both types of lattice distortion were significantly different on tensile properties. The combination with strength and ductility from high concentration of distorted lattice points was superior over that from low concentration ones even the latter had larger nominal atomic size difference and shear modulus difference. The evolution mechanisms on different mechanical properties from dilute alloys to concentrated alloys were elucidated and clarified under the large contrast of lattice distortion. The universal solid solution strengthening mechanism had been established.
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
不同晶格畸变对Ni-W稀溶液和CrFeNi、CoCrFeMnNi浓溶液拉伸性能的影响
溶质的晶格畸变主要是由于原子大小和与邻近原子化学键的差异。传统合金和高熵合金的晶格畸变效应是不同的,但缺乏澄清。在本研究中,fcc结构的Ni, Ni - 2at稀固溶体。%W和Ni-4at。设计了%W和等原子CrFeNi和CoCrFeMnNi金属的浓溶液来比较它们的拉伸性能。两种含W合金的晶格畸变均发生在大而强的W原子周围,但元素间原子尺寸和剪切模量相似的两种浓溶液在所有晶格位置都存在晶格畸变。结果表明,两种晶格畸变的趋势在拉伸性能上有显著差异。高浓度畸变晶格点对强度和延性的综合作用优于低浓度畸变晶格点,但后者的标称原子尺寸差异和剪切模量差异更大。在晶格畸变的大对比下,阐明了稀合金到浓合金不同力学性能的演化机理。建立了通用固溶强化机理。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
自引率
0.00%
发文量
0
期刊最新文献
Interfacial Microstructure and Mechanical Behavior of Low-Temperature Diffusion Bonded Mo/SS304 Joints Using Ni xCu 1-x Interlayers An Improved Fault Current Calculation Method and Protection Scheme of Doubly-Fed Induction Generator A Dual-Tunable Ultra-Broadband Terahertz Absorber Based on Graphene and Strontium Titanate Hydrogen Concentration and Hydrides in Zircaloy-4 During Cyclic Thermomechanical Loading Flaw-Insensitive Fracture of a Micrometer-Sized Brittle Metallic Glass
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1