Synthesis, Characterization and Dielectric properties of Nanoparticles of Cobalt Doped Ferrite (Cox Fe1-x Fe2 O4)

Ferrites, a recently uncovered category of materials, have found extensive application in various critical domains. Among them, cobalt ferrites stand out as hard magnetic materials with exceptional coercivity.. We successfully prepared cobalt ferrites by using nanocrystalline powers by Sol gel method. In our study Crystalline, Magnetic nanoparticles of Cobalt ferrites (Cox Fe1-x Fe2 O4) (x = 0.4, 0.5, 0.6, 0.8) were synthesized by Sol Gel Method using ferric chloride and cobalt nitrate with NaOH as a reactant. Structural characteristics of samples were determined by X-Ray diffraction and TEM. Particle size found between 8.8 nm to 14.26 nm using Debye Scherrer method. Lattice constant decreases as the value of ‘x’ increases. Dielectric properties were investigated using impedance analyser. The relative dielectric constant and loss tangents of ferrites a function of frequency (1kHz-30MHz) was investigated at room temperature, both parameter decreases as frequency increases.