Processing of Aqueous Graphite–Silicon Oxide Slurries and Its Impact on Rheology, Coating Behavior, Microstructure, and Cell Performance

The mixing process is the basis of the electrode microstructure, which defines key cell performance indicators. This work investigated the effects of varying the energy input within the mixing procedure on slurry rheology, coating behavior, mechanical and electrical properties of dry electrodes and electrochemical performance of cells fabricated from these negative electrodes. Energy input differences were achieved by varying the solids content within the mixing procedure; however, the final total solids content of the slurries was always the same. The slurries, produced with graphite and silicon oxide as active materials and carboxymethylcellulose (CMC) and styrene-butadiene rubber as binders, showed large differences in flow behavior which were explained by changes in CMC adsorption and mechanical degradation because of increasing energy input. Low shear viscosity and the degree of shear thinning decreased with increasing energy input, resulting in a narrower stability window for slot-die coating. The resistance between the electrode and current collector decreased as more CMC was adsorbed on the active material. Electrode adhesion drastically dropped at the highest energy input, presumably due to a change in SBR distribution. Despite these variations, all fabricated pouch cells demonstrated excellent electrochemical performance and a slight trend of increased charge capability was observed in cells prepared with higher energy input.