Influence of ultraviolet illumination on the corrosion behavior of 7A04 aluminum alloy in salt solutions with different pH values

This paper investigated the influence of ultraviolet (UV) illumination on the corrosion behavior of 7A04 aluminum alloy in 3.5% NaCl solutions with various pH values (, 7.0, and 10.0) using weight loss measurement, electrochemical methods, and surface analysis techniques. The research results indicated that the corrosion products of 7A04 alloy in salt solutions with different pH values all exhibited n-type semiconductor properties and could trigger the photovoltaic effect under UV illumination. Simultaneously, UV illumination reduced the compactness of the corrosion products, inhibited the enrichment of copper compounds (CuO), and promoted the generation of hydroxyl radicals in the solution. Therefore, UV illumination significantly accelerated the corrosion process of 7A04 alloy, with the overall acceleration effect ranking as follows: alkaline > neutral > acidic. In addition, the corrosion mechanism of 7A04 alloy in the test solutions with and without UV illumination was also discussed in this paper.