Sericin eco-friendly biomaterial as a spin finish in drawn textured PET yarn production

Purpose This paper aims to extracted sericin from the cocoons of Bombyx mori silkworms, and sericin powder was applied onto drawn textured polyethylene terephthalate (PET) yarns as a spin finish. The reactivity on the surface of PET yarns was analyzed through Fourier transform infrared spectrophotometry–attenuated total reflectance (FTIR-ATR) and dyeing with methylene blue as a reactive dye. Also, investigations were conducted on the effects of sericin, citrc acid (CA) (as a crosslinking agent), and sodium hypophosphite (as a catalyst) concentrations on some properties of false-twist textured PET yarns. Design/methodology/approach A false-twist texturing machine (Scragg-Shirley minibulk, England) was used with the draw ratio of 1.05, heating temperature of 120°C, texturing speed of 100 m min−1 and applied twist of 3,000 TPM. The aqueous extraction of sericin was carried out by the boiling of the raw silk in distilled water with L:R: 40:1 for 120 min. The aqueous solution was filtered with a filter paper to remove the impurities and insoluble fibroin. Finally, the sericin solution was freeze-dried to obtain the sericin powder. The sericin solution was applied on the drawn textured PET yarns using the “pad-dry-cure” method. Findings Sericin fixation onto the PET yarns was confirmed by FTIR-ATR. The results showed that there were no significant changes in the tensile strength, linear density, crimp contraction and crimp modulus, elongation at break and shrinkage. In contrast, a substantial increase was observed in moisture regain, vertical wicking, dye uptake and ultraviolet protection. There was also a reduction just in the electrical resistivity, in the presence of sericin. Originality/value Although sericin has been known to have numerous beneficial properties, its application in textile industry as a spin finish has not been reported yet.