Method of Suppressing Solidification Cracking by Laser Surface Melting and Epitaxial Growth Behavior for Directionally Solidified 247LC Superalloy

In this study, the relationship between solidification cracking and epitaxial growth behavior with the high-speed laser surface melting of a directionally solidified 247LC superalloys was fundamentally and metallurgically investigated, to develop a successful welding procedure for the next generation of gas turbine blades. Under typical laser surface melting conditions (scan speed: 50 mm/s, heat input: 40 J/mm), severe solidification cracking phenomena occurs. The key metallurgical factors of solidification cracking have been identified as solidification segregation-assisted pipeline diffusion behavior at the solidification grain boundary, and in the randomly formed polycrystalline melting zone microstructure. In addition, under extremely low heat input and high-speed laser beam scan conditions (scan speed: 1000 mm/s, heat input: 2 J/mm), an effective surface melting zone can be obtained within a single directionally solidified grain under a relatively high-energy beam density (65 J/mm2) using the characteristics of single-mode fiber lasers. Results reveal that the laser melting zone successfully shows a 99.9% epitaxial growth achievement ratio. Because of the superior epitaxial growth ratio within the laser surface melting zone, and the rapid solidification phenomena, formation of a solidification grain boundary and solidification segregation-assisted pipeline diffusion behavior can be suppressed. Finally, a solidification crack-free laser melting zone can thus be achieved.