Characterization of sound enamel and natural white spot lesions

Objective: To compare optical, morphological, chemical, and physical aspects of the sound enamel and white spot lesions (WSL) classified as ICDAS 2. Material and Methods: Seventeen human molars with one surface presenting WSL and a sound surface (2 x 2 mm window) were characterized by Quantitative light-induced fluorescence (QLF ® ), Optical coherence tomography (OCT), microhardness, and Raman spectroscopy. The ANOVA and Tukey’s test were used at 5% significance level. Results: The QLF comparison between distinct substrates yielded decreased ∆ Q (integrated fluorescence loss) of -15,37%mm 2 and -11,68% ∆ F (fluorescence loss) for WSL. The OCT detected mean lesion depth of 174,43 µm. ANOVA could not detect differences in the optical attenuation coefficient between the substrates (p>0.05). Lower microhardness measures were observed in WSL than on sound enamel (p<0.05). The Raman spectra showed four vibrational phosphate bands (v1, v2, v3, v4), where the highest peak was at 960.3 cm -1 (v1) for both substrates. However, a 40% decrease in phosphate (v1) was detected in WSL. The peak at 1071 cm -1 was higher for sound enamel, indicating the presence of a phosphate band instead of the B-type carbonate. The spectra showed higher intensity of the organic composition at 1295 cm -1 and 1450 cm -1 for WSL. Conclusion: Non-invasive QLF, OCT and Raman spectroscopy were able to distinguish differences in fluorescence, optical properties, and organic/inorganic components, respectively, between sound enamel and WSL, validated by the destructive microhardness analysis.