F. Trauter, J. Schanz, H. Riegel, T. Bernthaler, D. Goll, G. Schneider
{"title":"选择性激光熔炼块状纳米晶永磁体","authors":"F. Trauter, J. Schanz, H. Riegel, T. Bernthaler, D. Goll, G. Schneider","doi":"10.1515/pm-2021-0055","DOIUrl":null,"url":null,"abstract":"Abstract Fe-Nd-B powders were processed by additive manufacturing using laboratory scale selective laser melting to produce bulk nanocrystalline permanent magnets. The manufacturing process was carried out in a specially developed process chamber under Ar atmosphere. This resulted in novel types of microstructures with micrometer scale clusters of nanocrystalline hard magnetic grains. Owing to this microstructure, a maximum coercive field strength (coercivity) μ0Hc of 1.16 T, a remanence Jr of 0.58 T, and a maximum energy product (BH)max of 62.3 kJ/mm3could, for example, be obtained for the composition Nd16.5-Pr1.5-Zr2.6-Ti2.5-Co2.2-Fe65.9-B8.8.","PeriodicalId":20360,"journal":{"name":"Practical Metallography","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2021-10-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Bulk Nanocrystalline Permanent Magnets by Selective Laser Melting\",\"authors\":\"F. Trauter, J. Schanz, H. Riegel, T. Bernthaler, D. Goll, G. Schneider\",\"doi\":\"10.1515/pm-2021-0055\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Abstract Fe-Nd-B powders were processed by additive manufacturing using laboratory scale selective laser melting to produce bulk nanocrystalline permanent magnets. The manufacturing process was carried out in a specially developed process chamber under Ar atmosphere. This resulted in novel types of microstructures with micrometer scale clusters of nanocrystalline hard magnetic grains. Owing to this microstructure, a maximum coercive field strength (coercivity) μ0Hc of 1.16 T, a remanence Jr of 0.58 T, and a maximum energy product (BH)max of 62.3 kJ/mm3could, for example, be obtained for the composition Nd16.5-Pr1.5-Zr2.6-Ti2.5-Co2.2-Fe65.9-B8.8.\",\"PeriodicalId\":20360,\"journal\":{\"name\":\"Practical Metallography\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2021-10-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Practical Metallography\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1515/pm-2021-0055\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Practical Metallography","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1515/pm-2021-0055","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Bulk Nanocrystalline Permanent Magnets by Selective Laser Melting
Abstract Fe-Nd-B powders were processed by additive manufacturing using laboratory scale selective laser melting to produce bulk nanocrystalline permanent magnets. The manufacturing process was carried out in a specially developed process chamber under Ar atmosphere. This resulted in novel types of microstructures with micrometer scale clusters of nanocrystalline hard magnetic grains. Owing to this microstructure, a maximum coercive field strength (coercivity) μ0Hc of 1.16 T, a remanence Jr of 0.58 T, and a maximum energy product (BH)max of 62.3 kJ/mm3could, for example, be obtained for the composition Nd16.5-Pr1.5-Zr2.6-Ti2.5-Co2.2-Fe65.9-B8.8.