端缩水甘油酯聚氨酯的粘附性能和相分离行为

H. Hsia, C. Ma, D. Chen
{"title":"端缩水甘油酯聚氨酯的粘附性能和相分离行为","authors":"H. Hsia, C. Ma, D. Chen","doi":"10.1002/APMC.1994.052200112","DOIUrl":null,"url":null,"abstract":"2,3-Epoxy-1-propanol has been introduced into isocyanate-terminated polyurethane to form glycidyl-terminated polyurethane resins. A series of glycidyl-terminated polyurethanes based on hydroxyterminated poly(oxypropylene) (poly(oxypropylene) glycol, PPG), toluene diisocyanate (TDI), and 1,4-butanediol (BD) was synthesized with various PPG soft segment lengths (MW 700, 1000 and 2000) and soft segment concentrations (30, 50 and 70 wt.-%). The effects of glycidyl-terminated polyurethane on the adhesion properties and the phase separation were investigated. The adhision properties at liquid nitrogen temperature coincide with the phenomenon observed in the phase separation behavior of polyurethane. Differential scanning calorimetry (DSC) and infrared technique (IR) were used to assess the phase separation content. The enthalpy jump at the glass transition temperature (ΔCp) and the unique spectroscopic features in the NH and CO stretching regions were applied to characterized the phase separation behavior. It was found that the modified resins do not only show superior adhesion at liquid nitrogen temperature but also exhibit some unique properties, e.g., room temperature curing and good storage stability. \n \n \n \nDie Klebeeigenschaften und das Phasentrennungsverhalten von Polyurethanen aus „weichen” Poly(oxypropylen)-Einheiten (PPG) und „harten” Segmenten aus Toluoldiisocyanat (TDI) und 1,4-Butandiol (BD) wurden untersucht. Die Lange der PPG-Weichsegmente (PPG mit MW 700, 1000 bzw. 2000) sowie deren Konzentration (30, 50 and 70 Gew.-%) wurden variiert. Die Isocyanat-Endgruppen dieser PU-Harze wurden mit 2,3-Epoxy-1-propanol zu Glycidyl-Endgruppen umgesetzt. Die Klebeeigenschaften bei der Temperatur flussigen Stickstoffs folgen dem Phasentrennungsverhalten der Polyurethane. Die Phasentrennung wurde mit DSC-(Enthalpiesprung bei der Glasternperatur) und IR-Messungen (Veranderungen im Bereich der NH- und CO- Streckschwingungen) untersucht. Die rnodifizierten PU-Harze weisen neben verbesserter Haftung bei tiefen Temperaturen auch gute Lagerungseigenschaften sowie die Fahigkeit der Hartung bei Raumtemperatur auf.","PeriodicalId":7808,"journal":{"name":"Angewandte Makromolekulare Chemie","volume":"535 1","pages":"133-149"},"PeriodicalIF":0.0000,"publicationDate":"1994-03-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"16","resultStr":"{\"title\":\"Adhesion properties and phase separation behavior of glycidyl‐terminated polyurethanes\",\"authors\":\"H. Hsia, C. Ma, D. Chen\",\"doi\":\"10.1002/APMC.1994.052200112\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"2,3-Epoxy-1-propanol has been introduced into isocyanate-terminated polyurethane to form glycidyl-terminated polyurethane resins. A series of glycidyl-terminated polyurethanes based on hydroxyterminated poly(oxypropylene) (poly(oxypropylene) glycol, PPG), toluene diisocyanate (TDI), and 1,4-butanediol (BD) was synthesized with various PPG soft segment lengths (MW 700, 1000 and 2000) and soft segment concentrations (30, 50 and 70 wt.-%). The effects of glycidyl-terminated polyurethane on the adhesion properties and the phase separation were investigated. The adhision properties at liquid nitrogen temperature coincide with the phenomenon observed in the phase separation behavior of polyurethane. Differential scanning calorimetry (DSC) and infrared technique (IR) were used to assess the phase separation content. The enthalpy jump at the glass transition temperature (ΔCp) and the unique spectroscopic features in the NH and CO stretching regions were applied to characterized the phase separation behavior. It was found that the modified resins do not only show superior adhesion at liquid nitrogen temperature but also exhibit some unique properties, e.g., room temperature curing and good storage stability. \\n \\n \\n \\nDie Klebeeigenschaften und das Phasentrennungsverhalten von Polyurethanen aus „weichen” Poly(oxypropylen)-Einheiten (PPG) und „harten” Segmenten aus Toluoldiisocyanat (TDI) und 1,4-Butandiol (BD) wurden untersucht. Die Lange der PPG-Weichsegmente (PPG mit MW 700, 1000 bzw. 2000) sowie deren Konzentration (30, 50 and 70 Gew.-%) wurden variiert. Die Isocyanat-Endgruppen dieser PU-Harze wurden mit 2,3-Epoxy-1-propanol zu Glycidyl-Endgruppen umgesetzt. Die Klebeeigenschaften bei der Temperatur flussigen Stickstoffs folgen dem Phasentrennungsverhalten der Polyurethane. Die Phasentrennung wurde mit DSC-(Enthalpiesprung bei der Glasternperatur) und IR-Messungen (Veranderungen im Bereich der NH- und CO- Streckschwingungen) untersucht. Die rnodifizierten PU-Harze weisen neben verbesserter Haftung bei tiefen Temperaturen auch gute Lagerungseigenschaften sowie die Fahigkeit der Hartung bei Raumtemperatur auf.\",\"PeriodicalId\":7808,\"journal\":{\"name\":\"Angewandte Makromolekulare Chemie\",\"volume\":\"535 1\",\"pages\":\"133-149\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"1994-03-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"16\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Angewandte Makromolekulare Chemie\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1002/APMC.1994.052200112\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Angewandte Makromolekulare Chemie","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1002/APMC.1994.052200112","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 16

摘要

2,3-环氧-1-丙醇被引入到端异氰酸酯聚氨酯中,形成端缩水甘油聚氨酯树脂。以端羟基聚氧丙烯(聚氧丙烯乙二醇,PPG)、甲苯二异氰酸酯(TDI)和1,4-丁二醇(BD)为原料,合成了一系列端羟基聚氧丙烯(聚氧丙烯乙二醇,PPG)软段长度(分子量为700、1000和2000)和软段浓度(分子量为30、50和70 wt.-%)不同的端羟基环氧丙烷聚氨酯。研究了端缩水甘油酯对树脂粘附性能和相分离性能的影响。液氮温度下的吸附性能与聚氨酯的相分离行为一致。采用差示扫描量热法(DSC)和红外技术(IR)测定相分离含量。玻璃化转变温度下的焓跳(ΔCp)和NH和CO拉伸区独特的光谱特征被用于表征相分离行为。结果表明,改性后的树脂不仅在液氮温度下具有良好的附着力,而且具有室温固化和良好的储存稳定性等独特性能。聚氧丙烯-聚氧丙烯(PPG)和聚氧丙烯-聚氧丙烯(PPG)。PPG- weichsegment (PPG / MW 700,1000 bzw)2000) sowie deren konconcentration (30,50,70 Gew.-%) wurden品种。[2,3-环氧-1-丙醇][3-环氧-1-丙醇][6]。Die Klebeeigenschaften bei der temperature flussien Stickstoffs folgen dem Phasentrennungsverhalten der Polyurethane。2 . Die Phasentrennung wurde mit DSC-(Enthalpiesprung bei der glasternpernature)和IR-Messungen (Veranderungen im Bereich der NH- and CO- Streckschwingungen) untersucht。2 . Die nodifizierten PU-Harze weisen en verbesserter Haftung bei bebeteren temperature .(德国,德国,德国,德国,德国)
本文章由计算机程序翻译,如有差异,请以英文原文为准。
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Adhesion properties and phase separation behavior of glycidyl‐terminated polyurethanes
2,3-Epoxy-1-propanol has been introduced into isocyanate-terminated polyurethane to form glycidyl-terminated polyurethane resins. A series of glycidyl-terminated polyurethanes based on hydroxyterminated poly(oxypropylene) (poly(oxypropylene) glycol, PPG), toluene diisocyanate (TDI), and 1,4-butanediol (BD) was synthesized with various PPG soft segment lengths (MW 700, 1000 and 2000) and soft segment concentrations (30, 50 and 70 wt.-%). The effects of glycidyl-terminated polyurethane on the adhesion properties and the phase separation were investigated. The adhision properties at liquid nitrogen temperature coincide with the phenomenon observed in the phase separation behavior of polyurethane. Differential scanning calorimetry (DSC) and infrared technique (IR) were used to assess the phase separation content. The enthalpy jump at the glass transition temperature (ΔCp) and the unique spectroscopic features in the NH and CO stretching regions were applied to characterized the phase separation behavior. It was found that the modified resins do not only show superior adhesion at liquid nitrogen temperature but also exhibit some unique properties, e.g., room temperature curing and good storage stability. Die Klebeeigenschaften und das Phasentrennungsverhalten von Polyurethanen aus „weichen” Poly(oxypropylen)-Einheiten (PPG) und „harten” Segmenten aus Toluoldiisocyanat (TDI) und 1,4-Butandiol (BD) wurden untersucht. Die Lange der PPG-Weichsegmente (PPG mit MW 700, 1000 bzw. 2000) sowie deren Konzentration (30, 50 and 70 Gew.-%) wurden variiert. Die Isocyanat-Endgruppen dieser PU-Harze wurden mit 2,3-Epoxy-1-propanol zu Glycidyl-Endgruppen umgesetzt. Die Klebeeigenschaften bei der Temperatur flussigen Stickstoffs folgen dem Phasentrennungsverhalten der Polyurethane. Die Phasentrennung wurde mit DSC-(Enthalpiesprung bei der Glasternperatur) und IR-Messungen (Veranderungen im Bereich der NH- und CO- Streckschwingungen) untersucht. Die rnodifizierten PU-Harze weisen neben verbesserter Haftung bei tiefen Temperaturen auch gute Lagerungseigenschaften sowie die Fahigkeit der Hartung bei Raumtemperatur auf.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
自引率
0.00%
发文量
0
期刊最新文献
Copolymerization of styrene with butadiene using methyl tert‐butyl ether as active center modifier Comparison of poly(2,5-dibutoxy-p-phenylenevinylene)s synthesized by two different methods Electro‐optic birefringence and scattering of concentrated solutions of ethylcellulose Photovieillissement d'un copolymère d'éthylène et d'acétate de vinyle en présence de sueur artificielle. II. Evolution morphologique N‐Oxyl‐kontrollierte radikalische Lösungspolymerisation von Styrol
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1