Electrical Conduction in PbMoO4 Crystals

The application of an electric field (300 V/cm) on PbMoO4 crystals at direct contacts generates a coloration spreading from the anode. The absorption at about 2.2 eV vanishes after annealing in air. The current-voltage characteristic exhibits a linear relationship under special conditions. Annealing in reducing nitrogen atmosphere drastically enhances the conductivity and gives rise to the occurrence of a quadratic characteristic. Oxygen vacancies are assumed to be involved in trapping processes during the injection of carriers. A narrow peak in the photoconductivity spectrum at 380 nm is ascribed to the transition of an electron from the 6s2 state of the lead ion to the 2e molecular orbital of the oxocomplex ion with a subsequent thermal activation. Some other bands in the longwave region are correlated to (MoO4)3− centers and oxygen vacancies. Das Anlegen eines elektrischen Feldes (300 V/cm) an PbMoO4-Kristallen bei direkten Kontakten verursacht cine Verfarbung, die sich von der Anode her ausbreitet. Die Absorption bei etwa 2,2 eV verschwindet nach Tempern in Luft. Die Strom-Spannungs-Kennlinie zeigt unter gewissen Bedingungen einen linearen Verlauf. Das Ausheizen in reduzierender Stickstoffatmosphare erhoht die Leitfahigkeit drastisch und labt eine quadratische Kennlinie erkennen. Es wird deshalb angenommen, ds wahrend der Injektion von Ladungstragern Sauerstoffleerstellen an Trapping-Vorgaangen beteiligt sind. Die Photoleitfahigkeit zeigt einen schmalen Peak bei 380 nm, der dem Ubergang eines Elektrons vom 682-Zustand des Bleiions zum 2e-Molekulorbital des Oxokomplexions zugeschrieben wird mit einer anschliesenden thermischen Aktivierung. Andere Banden im langwelligen Bereich werden mit (MoO4)3−Zentren und Sauerstoffleerstellen in Verbindung gebracht.