V. Arantes, Lisa Genova, P. B. Guimarães, C. Fortulan, J. Vleugels
{"title":"NbC含量对氧化铝/铌合金刀具耐磨性的影响","authors":"V. Arantes, Lisa Genova, P. B. Guimarães, C. Fortulan, J. Vleugels","doi":"10.1590/1980-5373-MR-2020-0552","DOIUrl":null,"url":null,"abstract":"Abstract Wear resistance is a fundamental property which defines the lifetime of cutting tools, but the investigation of wear performance of alternative hard materials for traditional WC-Co composites are recent. The present work evaluated the pin-on-disk wear behavior and mechanical properties, i.e., hardness and fracture toughness of spark plasma sintered Al2O3 matrix composites with additions of 5, 15, 25 or 30%wt of niobium carbide NbC. The wear resistance was observed to increase as a function of the NbC content, even though the hardness reached a plateau at 25%wt NbC. The composite behavior was compared to that of other alumina composite tool materials proving to be a promising material for applications such as ceramic cutting tools. The composition A95N5 presented the best combination of values of wear rate: 8.9 mm3/N.m, hardness equal to (17.36±1.72) GPa and fracture toughness of (3.2±0.6) MPa. m1/2.","PeriodicalId":18331,"journal":{"name":"Materials Research-ibero-american Journal of Materials","volume":null,"pages":null},"PeriodicalIF":1.5000,"publicationDate":"2021-05-28","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"1","resultStr":"{\"title\":\"Influence of NbC Content on the Wear Resistance of Alumina/Niobium Carbide Tools\",\"authors\":\"V. Arantes, Lisa Genova, P. B. Guimarães, C. Fortulan, J. Vleugels\",\"doi\":\"10.1590/1980-5373-MR-2020-0552\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Abstract Wear resistance is a fundamental property which defines the lifetime of cutting tools, but the investigation of wear performance of alternative hard materials for traditional WC-Co composites are recent. The present work evaluated the pin-on-disk wear behavior and mechanical properties, i.e., hardness and fracture toughness of spark plasma sintered Al2O3 matrix composites with additions of 5, 15, 25 or 30%wt of niobium carbide NbC. The wear resistance was observed to increase as a function of the NbC content, even though the hardness reached a plateau at 25%wt NbC. The composite behavior was compared to that of other alumina composite tool materials proving to be a promising material for applications such as ceramic cutting tools. The composition A95N5 presented the best combination of values of wear rate: 8.9 mm3/N.m, hardness equal to (17.36±1.72) GPa and fracture toughness of (3.2±0.6) MPa. m1/2.\",\"PeriodicalId\":18331,\"journal\":{\"name\":\"Materials Research-ibero-american Journal of Materials\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":1.5000,\"publicationDate\":\"2021-05-28\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"1\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Materials Research-ibero-american Journal of Materials\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://doi.org/10.1590/1980-5373-MR-2020-0552\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Research-ibero-american Journal of Materials","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1590/1980-5373-MR-2020-0552","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
Influence of NbC Content on the Wear Resistance of Alumina/Niobium Carbide Tools
Abstract Wear resistance is a fundamental property which defines the lifetime of cutting tools, but the investigation of wear performance of alternative hard materials for traditional WC-Co composites are recent. The present work evaluated the pin-on-disk wear behavior and mechanical properties, i.e., hardness and fracture toughness of spark plasma sintered Al2O3 matrix composites with additions of 5, 15, 25 or 30%wt of niobium carbide NbC. The wear resistance was observed to increase as a function of the NbC content, even though the hardness reached a plateau at 25%wt NbC. The composite behavior was compared to that of other alumina composite tool materials proving to be a promising material for applications such as ceramic cutting tools. The composition A95N5 presented the best combination of values of wear rate: 8.9 mm3/N.m, hardness equal to (17.36±1.72) GPa and fracture toughness of (3.2±0.6) MPa. m1/2.