Hydrolytic stability and mechanical properties of poly(ester urethanes)

The effect of hydrolysis time at 70°C on molar mass and mechanical properties of commercial poly(ester urethanes), i.e., Estanes 54600, 54610, and 54650, was analyzed. Kinetics of hydrolysis is plausibly described in terms of a first-order reaction with an average induction period of about 7 days. The resulting reduction of molar mass brought about a significant decrease in ultimate properties, particularly in stress at break and tensile energy to break, while elastic properties were affected much less. A quantitative correlation between relative changes in tensile strength and molar mass was attempted. Hydrolysis resistance of Estanes decreasing in the succession 54650 > 54600 > 54610 was related to their chemical composition. Der Einflus der Hydrolysedauer bei 70°C auf die Molmasse und die mechanischen Eigenschaften handelsublicher Polyesterurethane (Estane 54600, 54610 und 54650) wurde untersucht. Die Kinetik der Hydrolyse last sich als Reaktion erster Ordnung mit einer mittleren Induktionsperiode von etwa 7 Tagen beschreiben. Die resultierende Molmassenabnahme verursacht eine signifikante Verschlechterung der Eigenschaften, insbesondere der Bruchdehnung und der Zugarbeit bis zum Bruch, wahrend die elastischen Eigenschaften weit weniger beeintrachtigt wurden. Eine quantitative Beziehung zwischen der relativen Anderung der Zugfestigkeit und der Molmasse wird vorgeschlagen. Die in der Reihenfolge 54650 > 54600 > 54610 abnehmende Hydrolysebestandigkeit der Estane last sich mit Unterschieden in deren chemischer Zusammensetzung erklaren.