Synthesis of hydrophilic elastomers by radiation grafting

Radiation grafting of acrylic acid (AAc) onto ethylene-propylene rubber (EPR) to obtain hydrophilic elastomers has been investigated. It was found that by addition of alcohol (methanol and 1-propanol) into water as solvent for grafting the degree of grafting increased and formation of homopolymer was retarded. The grafting by addition of alcohol occurred even in deeper portions of the film compared with no addition of alcohol. Grafting rate differed largely with propylene contents in the EPR. Graft polymerization occurred easily in EPR of lower propylene contents such as 22%. Before introducing AAc in grafting the stability of EPR radicals of lower propylene contents was higher in comparison with other components. Water absorption of EPR increased linearly with increasing grafting yield. Die strahleninduzierte Pfropfung von Acrylsaure auf Ethylen-Propylen-Kautschuk (EPR) wurde untersucht. Es wurde gefunden, das die Pfropfungsgrade bei Zugabe von Alkohol (Methanol und Isopropanol) abnahmen und die Bildung der Homopolymeren verzogert wurde. Bei Zugabe von Alkohol fand Pfropfung auch im Innern des Filmes statt. Die Pfropfungsgeschwindigkeit war sehr stark vom Propylengehalt im EPR abhangig. Die Pfropfungspolymerisation fand bei kleinen Propylengehalten, z. B. bei 22%, leichter statt. Die Stabilitat der Radikale mit niedrigeren Propylengehalten war hoher als die der anderen. Die Wasseraufnahme der gepfropften Filme stiegen linear mit dem Pfropfungsgrad an.