{"title":"辐照交联醋酸乙烯/废轮胎粉尘共混物的性能研究","authors":"Z.A. Anis Sakinah, C. Ratnam, A. Luqman Chuah, T. Yaw","doi":"10.1177/0095244311398629","DOIUrl":null,"url":null,"abstract":"The effect of irradiation on a 90/10 ethylene vinyl acetate/waste tire dust (EVA/WTD) blend was studied in the presence of 4 phr trimethylolpropane triacrylate (TMPTA) or tripropyleneglycol diacrylate (TPGDA). The blend was irradiated using a 3.0-MeV electron beam machine at 0, 50, 100, 150, and 200 kGy irradiation doses. The properties studied include gel content, tensile properties, hardness, morphology, and dynamic mechanical properties. The result revealed that the increment in irradiation doses will increase the percentage of gel content. The gel content further increased with the introduction of TMPTA and TPGDA. This is attributed to the increase in crosslink density. Tensile properties of EVA/WTD blend increase with the introduction of irradiation except for elongation at break. The tensile-fractured surface of EVA/WTD blends showed ductile type of failure upon irradiation of the blends in the presence of crosslinking agent. One glass transition temperature obtained from dynamic mechanical analysis for 90/10 EVA/WTD blend after irradiation indicates that compatibility between EVA and WTD phases increased.","PeriodicalId":15644,"journal":{"name":"Journal of Elastomers and Plastics","volume":"55 1","pages":"239 - 256"},"PeriodicalIF":1.4000,"publicationDate":"2011-05-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"19","resultStr":"{\"title\":\"Performance of Irradiated and Crosslinked Ethylene Vinyl Acetate/Waste Tire Dust Blend\",\"authors\":\"Z.A. Anis Sakinah, C. Ratnam, A. Luqman Chuah, T. Yaw\",\"doi\":\"10.1177/0095244311398629\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The effect of irradiation on a 90/10 ethylene vinyl acetate/waste tire dust (EVA/WTD) blend was studied in the presence of 4 phr trimethylolpropane triacrylate (TMPTA) or tripropyleneglycol diacrylate (TPGDA). The blend was irradiated using a 3.0-MeV electron beam machine at 0, 50, 100, 150, and 200 kGy irradiation doses. The properties studied include gel content, tensile properties, hardness, morphology, and dynamic mechanical properties. The result revealed that the increment in irradiation doses will increase the percentage of gel content. The gel content further increased with the introduction of TMPTA and TPGDA. This is attributed to the increase in crosslink density. Tensile properties of EVA/WTD blend increase with the introduction of irradiation except for elongation at break. The tensile-fractured surface of EVA/WTD blends showed ductile type of failure upon irradiation of the blends in the presence of crosslinking agent. One glass transition temperature obtained from dynamic mechanical analysis for 90/10 EVA/WTD blend after irradiation indicates that compatibility between EVA and WTD phases increased.\",\"PeriodicalId\":15644,\"journal\":{\"name\":\"Journal of Elastomers and Plastics\",\"volume\":\"55 1\",\"pages\":\"239 - 256\"},\"PeriodicalIF\":1.4000,\"publicationDate\":\"2011-05-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"19\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Journal of Elastomers and Plastics\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://doi.org/10.1177/0095244311398629\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Elastomers and Plastics","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1177/0095244311398629","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
Performance of Irradiated and Crosslinked Ethylene Vinyl Acetate/Waste Tire Dust Blend
The effect of irradiation on a 90/10 ethylene vinyl acetate/waste tire dust (EVA/WTD) blend was studied in the presence of 4 phr trimethylolpropane triacrylate (TMPTA) or tripropyleneglycol diacrylate (TPGDA). The blend was irradiated using a 3.0-MeV electron beam machine at 0, 50, 100, 150, and 200 kGy irradiation doses. The properties studied include gel content, tensile properties, hardness, morphology, and dynamic mechanical properties. The result revealed that the increment in irradiation doses will increase the percentage of gel content. The gel content further increased with the introduction of TMPTA and TPGDA. This is attributed to the increase in crosslink density. Tensile properties of EVA/WTD blend increase with the introduction of irradiation except for elongation at break. The tensile-fractured surface of EVA/WTD blends showed ductile type of failure upon irradiation of the blends in the presence of crosslinking agent. One glass transition temperature obtained from dynamic mechanical analysis for 90/10 EVA/WTD blend after irradiation indicates that compatibility between EVA and WTD phases increased.
期刊介绍：
The Journal of Elastomers and Plastics is a high quality peer-reviewed journal which publishes original research on the development and marketing of elastomers and plastics and the area in between where the characteristics of both extremes are apparent. The journal covers: advances in chemistry, processing, properties and applications; new information on thermoplastic elastomers, reinforced elastomers, natural rubbers, blends and alloys, and fillers and additives.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们