4-乙烯基吡啶接枝SBS带电镶嵌膜的合成及性能研究

G. Hsiue, Z. Yeh
{"title":"4-乙烯基吡啶接枝SBS带电镶嵌膜的合成及性能研究","authors":"G. Hsiue, Z. Yeh","doi":"10.1002/APMC.1987.051530103","DOIUrl":null,"url":null,"abstract":"The grafting of 4-vinyl pyridine onto styrene-butadiene-styrene triblock copolymer by irradiation was studied. Cationic and anionic groups were introduced by sulfonation and methylation to obtain a charged mosaic membrane. \n \n \n \nThe experiments showed an increased rate of grafting with the increase of irradation dose. The best concentration of monomer was at 20%. \n \n \n \nAfter grafting, the contact angle and the water content were tested and morphology studies were performed. \n \n \n \nFurthermore, the tensile strength of this membrane increased with increased percentage of grafting. After testing, the charged mosaic membrane had a reduced potential. Its anionic and cationic exchange capacitites were between 0.12 to 0.13 meq/g, and 0.24 to 0.343 meq/g, respectively. The ratio of exchanged capacity was up to 0.509. KCI and urea can be separated by dialysis. In the determination of a piezodialysis, the salt enrichment reached a percentage of 10.3. \n \n \n \n4-Vinylpyridin wurde durch Bestrahlung auf ein Styrol-Butadien-Styrol-Blockcopolymeres aufgepfropft. Kationische und anionische Gruppen wurden durch Sulfonierung und Methylierung eingefuhrt, wobei eine Membran mit Ladungsmosaik entstand. \n \n \n \nDie Experimente zeigten, das die Pfropfgeschwindigkeit mit der Strahlendosis anstieg. Die gunstigste Monomerkonzentration lag bei 20%. \n \n \n \nNach der Pfropfung wurden der Kontaktwinkel und der Wassergehalt bestimmt sowie Morphologiestudien unternommen. Ferner wurden Zug-Dehnungsuntersuchungen durchgefuhrt sowie das Potential, die Ionenaustauschkapazitaten und das Austauschkapazitatsverhaltnis der Membranen untersucht. KCl und Harnstoff konnen mittels solcher Membranen getrennt, und eine Salzanreicherung in einer Druckdialyse kann erreicht werden.","PeriodicalId":7808,"journal":{"name":"Angewandte Makromolekulare Chemie","volume":"24 1","pages":"33-53"},"PeriodicalIF":0.0000,"publicationDate":"1987-08-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"6","resultStr":"{\"title\":\"Synthesis and properties of 4-vinyl pyridine grafted SBS used as charged mosaic membrane\",\"authors\":\"G. Hsiue, Z. Yeh\",\"doi\":\"10.1002/APMC.1987.051530103\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The grafting of 4-vinyl pyridine onto styrene-butadiene-styrene triblock copolymer by irradiation was studied. Cationic and anionic groups were introduced by sulfonation and methylation to obtain a charged mosaic membrane. \\n \\n \\n \\nThe experiments showed an increased rate of grafting with the increase of irradation dose. The best concentration of monomer was at 20%. \\n \\n \\n \\nAfter grafting, the contact angle and the water content were tested and morphology studies were performed. \\n \\n \\n \\nFurthermore, the tensile strength of this membrane increased with increased percentage of grafting. After testing, the charged mosaic membrane had a reduced potential. Its anionic and cationic exchange capacitites were between 0.12 to 0.13 meq/g, and 0.24 to 0.343 meq/g, respectively. The ratio of exchanged capacity was up to 0.509. KCI and urea can be separated by dialysis. In the determination of a piezodialysis, the salt enrichment reached a percentage of 10.3. \\n \\n \\n \\n4-Vinylpyridin wurde durch Bestrahlung auf ein Styrol-Butadien-Styrol-Blockcopolymeres aufgepfropft. Kationische und anionische Gruppen wurden durch Sulfonierung und Methylierung eingefuhrt, wobei eine Membran mit Ladungsmosaik entstand. \\n \\n \\n \\nDie Experimente zeigten, das die Pfropfgeschwindigkeit mit der Strahlendosis anstieg. Die gunstigste Monomerkonzentration lag bei 20%. \\n \\n \\n \\nNach der Pfropfung wurden der Kontaktwinkel und der Wassergehalt bestimmt sowie Morphologiestudien unternommen. Ferner wurden Zug-Dehnungsuntersuchungen durchgefuhrt sowie das Potential, die Ionenaustauschkapazitaten und das Austauschkapazitatsverhaltnis der Membranen untersucht. KCl und Harnstoff konnen mittels solcher Membranen getrennt, und eine Salzanreicherung in einer Druckdialyse kann erreicht werden.\",\"PeriodicalId\":7808,\"journal\":{\"name\":\"Angewandte Makromolekulare Chemie\",\"volume\":\"24 1\",\"pages\":\"33-53\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"1987-08-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"6\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Angewandte Makromolekulare Chemie\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1002/APMC.1987.051530103\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Angewandte Makromolekulare Chemie","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1002/APMC.1987.051530103","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 6

摘要

研究了4-乙烯基吡啶在苯乙烯-丁二烯-苯乙烯三嵌段共聚物上的辐照接枝反应。通过磺化和甲基化引入阳离子和阴离子基,得到带电荷的马赛克膜。实验表明,随着辐照剂量的增加,接枝率增加。单体的最佳浓度为20%。接枝后,测定了接触角和含水量,并进行了形貌研究。此外,随着接枝率的增加,膜的拉伸强度也有所提高。经测试,带电荷的马赛克膜电位降低。其阴离子交换容量为0.12 ~ 0.13 meq/g,阳离子交换容量为0.24 ~ 0.343 meq/g。交换容量比达到0.509。KCI和尿素可通过透析分离。在压析的测定中,盐的富集达到了百分之10.3。聚苯乙烯-丁二烯-聚苯乙烯嵌段共聚物;国家和阴离子集团的研究表明,该集团的研究方向是磺化和甲基化。Die Experimente zeigten, Die Pfropfgeschwindigkeit mit der Strahlendosis anstig。单体的选矿滞后率为20%。我们的研究对象是我们的形态学研究对象和我们的研究对象。在此基础上,研究人员提出了一种新的研究方法,即“电位”、“膜”和“膜”。KCl和Harnstoff konnen mittel, solcher膜的制备,和Salzanreicherung在iner药物透析中的应用。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Synthesis and properties of 4-vinyl pyridine grafted SBS used as charged mosaic membrane
The grafting of 4-vinyl pyridine onto styrene-butadiene-styrene triblock copolymer by irradiation was studied. Cationic and anionic groups were introduced by sulfonation and methylation to obtain a charged mosaic membrane. The experiments showed an increased rate of grafting with the increase of irradation dose. The best concentration of monomer was at 20%. After grafting, the contact angle and the water content were tested and morphology studies were performed. Furthermore, the tensile strength of this membrane increased with increased percentage of grafting. After testing, the charged mosaic membrane had a reduced potential. Its anionic and cationic exchange capacitites were between 0.12 to 0.13 meq/g, and 0.24 to 0.343 meq/g, respectively. The ratio of exchanged capacity was up to 0.509. KCI and urea can be separated by dialysis. In the determination of a piezodialysis, the salt enrichment reached a percentage of 10.3. 4-Vinylpyridin wurde durch Bestrahlung auf ein Styrol-Butadien-Styrol-Blockcopolymeres aufgepfropft. Kationische und anionische Gruppen wurden durch Sulfonierung und Methylierung eingefuhrt, wobei eine Membran mit Ladungsmosaik entstand. Die Experimente zeigten, das die Pfropfgeschwindigkeit mit der Strahlendosis anstieg. Die gunstigste Monomerkonzentration lag bei 20%. Nach der Pfropfung wurden der Kontaktwinkel und der Wassergehalt bestimmt sowie Morphologiestudien unternommen. Ferner wurden Zug-Dehnungsuntersuchungen durchgefuhrt sowie das Potential, die Ionenaustauschkapazitaten und das Austauschkapazitatsverhaltnis der Membranen untersucht. KCl und Harnstoff konnen mittels solcher Membranen getrennt, und eine Salzanreicherung in einer Druckdialyse kann erreicht werden.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
自引率
0.00%
发文量
0
期刊最新文献
Copolymerization of styrene with butadiene using methyl tert‐butyl ether as active center modifier Comparison of poly(2,5-dibutoxy-p-phenylenevinylene)s synthesized by two different methods Electro‐optic birefringence and scattering of concentrated solutions of ethylcellulose Photovieillissement d'un copolymère d'éthylène et d'acétate de vinyle en présence de sueur artificielle. II. Evolution morphologique N‐Oxyl‐kontrollierte radikalische Lösungspolymerisation von Styrol
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1