{"title":"透明电极的腐蚀研究","authors":"A. Maged, L. A. M. Nada","doi":"10.2478/adms-2022-0005","DOIUrl":null,"url":null,"abstract":"Abstract This work reports a study of corrosion lifetime of transparent electrodes deposited on the microscopic glass substrate. A procedure was developed for obtaining the transparent electrode by spray method. The corrosion lifetime variation in the presence of 1.5 M NaOH medium chemically degraded at room temperature before and after gamma irradiation was determined by measuring the evolution of the structure, electrical and optical characteristics. The mean values of transmittance up to 25 month before and after irradiation were calculated 91% ±6% and 96±7%, respectively. The average value of resistivity after corrosion and age time after γ-irradiation was 0.016±9% Ω.cm and 0.017± 4% at 1.0 kHz. No significant changes observed for 27 hr corrosion and 25 month age time of the transparent electrodes in NaOH solution.","PeriodicalId":7327,"journal":{"name":"Advances in Materials Science","volume":null,"pages":null},"PeriodicalIF":1.5000,"publicationDate":"2022-06-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"1","resultStr":"{\"title\":\"Corrosion of Transparent Electrodes Study\",\"authors\":\"A. Maged, L. A. M. Nada\",\"doi\":\"10.2478/adms-2022-0005\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Abstract This work reports a study of corrosion lifetime of transparent electrodes deposited on the microscopic glass substrate. A procedure was developed for obtaining the transparent electrode by spray method. The corrosion lifetime variation in the presence of 1.5 M NaOH medium chemically degraded at room temperature before and after gamma irradiation was determined by measuring the evolution of the structure, electrical and optical characteristics. The mean values of transmittance up to 25 month before and after irradiation were calculated 91% ±6% and 96±7%, respectively. The average value of resistivity after corrosion and age time after γ-irradiation was 0.016±9% Ω.cm and 0.017± 4% at 1.0 kHz. No significant changes observed for 27 hr corrosion and 25 month age time of the transparent electrodes in NaOH solution.\",\"PeriodicalId\":7327,\"journal\":{\"name\":\"Advances in Materials Science\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":1.5000,\"publicationDate\":\"2022-06-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"1\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Advances in Materials Science\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.2478/adms-2022-0005\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Advances in Materials Science","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.2478/adms-2022-0005","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 1
摘要
摘要本文报道了沉积在微观玻璃基板上的透明电极的腐蚀寿命的研究。提出了一种喷雾法制备透明电极的方法。通过测量结构、电学和光学特性的演变,确定了在室温下化学降解的1.5 M NaOH介质存在前后的腐蚀寿命变化。照射前后25个月的平均透光率分别为91%±6%和96±7%。腐蚀后电阻率和γ辐照时效时间的平均值为0.016±9% Ω。0.017±4%在1.0 kHz。在NaOH溶液中腐蚀27小时和时效25个月,透明电极无明显变化。
Abstract This work reports a study of corrosion lifetime of transparent electrodes deposited on the microscopic glass substrate. A procedure was developed for obtaining the transparent electrode by spray method. The corrosion lifetime variation in the presence of 1.5 M NaOH medium chemically degraded at room temperature before and after gamma irradiation was determined by measuring the evolution of the structure, electrical and optical characteristics. The mean values of transmittance up to 25 month before and after irradiation were calculated 91% ±6% and 96±7%, respectively. The average value of resistivity after corrosion and age time after γ-irradiation was 0.016±9% Ω.cm and 0.017± 4% at 1.0 kHz. No significant changes observed for 27 hr corrosion and 25 month age time of the transparent electrodes in NaOH solution.