{"title":"氢在阳极应力腐蚀开裂中作用的热力学分析","authors":"L. Qiao, X. Mao","doi":"10.1016/0956-7151(95)00090-I","DOIUrl":null,"url":null,"abstract":"<div><p>A synergistic effect of hydrogen and stress on a corrosion rate was analyzed with thermodynamics. The results showed that an interaction of stress and hydrogen could increase the corrosion rate remarkably. Stress corrosion cracking (SCC) of austenitic stainless steel (ASS) was investigated in boiling chloride solution to confirm the analysis. Hydrogen could be introduced into the specimen and concentrated at the crack tip during SCC in boiling LiCl solution (143°C). The concentrating factor is about 3 which is consistent with calculated results according to stress induced diffusion.</p></div>","PeriodicalId":100018,"journal":{"name":"Acta Metallurgica et Materialia","volume":"43 11","pages":"Pages 4001-4006"},"PeriodicalIF":0.0000,"publicationDate":"1995-11-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://sci-hub-pdf.com/10.1016/0956-7151(95)00090-I","citationCount":"33","resultStr":"{\"title\":\"Thermodynamic analysis on the role of hydrogen in anodic stress corrosion cracking\",\"authors\":\"L. Qiao, X. Mao\",\"doi\":\"10.1016/0956-7151(95)00090-I\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><p>A synergistic effect of hydrogen and stress on a corrosion rate was analyzed with thermodynamics. The results showed that an interaction of stress and hydrogen could increase the corrosion rate remarkably. Stress corrosion cracking (SCC) of austenitic stainless steel (ASS) was investigated in boiling chloride solution to confirm the analysis. Hydrogen could be introduced into the specimen and concentrated at the crack tip during SCC in boiling LiCl solution (143°C). The concentrating factor is about 3 which is consistent with calculated results according to stress induced diffusion.</p></div>\",\"PeriodicalId\":100018,\"journal\":{\"name\":\"Acta Metallurgica et Materialia\",\"volume\":\"43 11\",\"pages\":\"Pages 4001-4006\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"1995-11-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://sci-hub-pdf.com/10.1016/0956-7151(95)00090-I\",\"citationCount\":\"33\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Acta Metallurgica et Materialia\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/095671519500090I\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Acta Metallurgica et Materialia","FirstCategoryId":"1085","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/095671519500090I","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Thermodynamic analysis on the role of hydrogen in anodic stress corrosion cracking
A synergistic effect of hydrogen and stress on a corrosion rate was analyzed with thermodynamics. The results showed that an interaction of stress and hydrogen could increase the corrosion rate remarkably. Stress corrosion cracking (SCC) of austenitic stainless steel (ASS) was investigated in boiling chloride solution to confirm the analysis. Hydrogen could be introduced into the specimen and concentrated at the crack tip during SCC in boiling LiCl solution (143°C). The concentrating factor is about 3 which is consistent with calculated results according to stress induced diffusion.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们