Phase Diagram and Lattice Parameter Values for the Hg 2x(AgIn) 1-x Te 2 Alloys

Abstract

Polycrystalline samples of Hg2x(AgIn)1−xTe2 alloys are prepared by the melt and anneal technique. Differential thermal analysis (DTA) measurements are carried out on the alloys and the T(x) diagram determined. Guinier X-ray powder photographs are used to show the equilibrium conditions and to give lattice parameter values. Only two single phase solid fields, the zincblende and chalcopyrite fields are found to exist in the diagram. The form of the solidus curve bounding a wide two-phase liquid plus solid field shows that the section is not pseudobinary. Microscopic and DTA data show the presence of the dissociated phase in the grain boundaries of the zinc-blende phase at temperatures below 400 °C. Polykristalline Proben von Hg2x(AgIn)1−xTe2-Legierungen werden mittels Schmelz- und Temperungstechnik prapariert. Thermische Differentialanalyse (DTA) wird an den Legierungen durchgefuhrt und das T(x)-Diagramm bestimmt. Guinier-Rontgen-Pulverphotographien werden benutzt, um die Gleichgewichstbedingungen zu zeigen und Gitterparameterwerte anzugeben. Es wird gefunden, das nur zwei Ein-Phasen-Festkorperfelder, die Zinkblende- und Chalkopyrit-Felder in dem Diagramm existieren. Die Form der Soliduskurve, die ein weites Zweiphasen-Flussigkeits- und Festkorperfeld begrenzt, zeigt, das der Abschnitt nicht pseudobinar ist. Mikroskopische und DTA-Werte zeigen die Anwesenheit der dissoziierten Phase in den Korngrenzen der Zinkblendephase bei Temperaturen unterhalb 400 °C.