THE INFLUENCE OF HYDROPHOBIC COATING ON THE EFFICIENCY OF FIRE PROTECTION OF TEXTILE MATERIALS

Abstract

Abstract. The analysis of fire-retardant materials for fabrics is carried out and it is established that the paucity of data for explanation and description of the process of fire protection, neglect of elastic coatings, leads to ignition of fabric structures under the action of flame. The development of reliable methods for studying the conditions of fire protection of fabrics leads to the creation of new types of fire protective materials. Therefore, it becomes necessary to determine the conditions for the formation of a barrier both for high temperatures and for leaching in the presence of precipitation and to establish a mechanism for inhibition of these processes. In this regard, full-scale tests were carried out and it was found out that when the flame is applied to untreated model samples of tent elements made of canvas fabric, the surface ignites and spreads the flame, which leads to their complete combustion within 105...120 s, instead, the model The fire-resistant sample of tent elements did not catch fire when ignited with a gasoline-based substance, and the flame did not spread. In this case, the final combustion was recorded for 3 c and the swelling of the protective coating reached 3...5 mm, and the surface was charred on an area of about 80% from the inside. When tested for fire retardant efficiency for a fire-resistant sample treated with a water repellent (5 % solution of GDJ-94), a decrease in efficiency and carbonization of the material was recorded, which amounted to 100%, and for a fire-resistant sample treated with a water repellent (5 % solution), a decrease in efficiency was recorded due to the combustion of paraffin and local burnout of the material, and carbonization was 100 %. Obviously, such a mechanism of influence of the fire-retardant coating is the factor regulating the process, which preserves the integrity of the object. Thus, there is reason to argue about the possibility of targeted regulation of the processes of fire protection of the fabric by applying coatings capable of forming a protective layer on the surface of the material, which inhibits the rate of heat penetration.