Addition of Modifying Agents vs Basic Functional Properties of Moldings Made of ABS

Abstract

Unconventional injection methods include i.e. blowing injection that allows for production of moldings with a lower weight while maintaining mechanical properties of detail. Due to the fact that most polymers are dyed at the processing stage, it is important to examine the simultaneous effect of blowing and colorbatch, as well as variable processing conditions, on the functional properties of moldings made of the most popular construction material, i.e. ABS. Samples were made of ABS polymer without and with the addition of a colorbatch containing brown pigment on ABS matrix, and blowing agent. Variable processing conditions were: mold and injection temperature, holding pressure and time. Other parameters were constant. Samples were tested for basic functional properties such as color, gloss, mass, density and thickness. Moldings produced with a higher blowing agent content and a higher injection temperature were characterized by lower mass. No significant influence of processing parameters and content of colorbatch on mass of samples was found. Blowing agent has no significant impact on thickness of moldings, regardless of processing conditions. Addition of a colorbatch influenced samples’ gloss. Increase in colorbatch and blowing agent content and mold temperature allow to obtain moldings with a higher surface gloss. Colorbatch also changed color of samples – a decrease in luminance L even by about 40% and great changes in parameters “a” and slight changes in parameter “b”. It was found that blowing agent content had the greatest influence on density of moldings. Injection temperature and colorbatch, do not significantly affect density of moldings.