Crack initiation during environment-induced cracking of metals: current status

Abstract

Abstract Environment-induced cracking (EIC) research spanning the last 80 years for ferrous and non-ferrous metals in aqueous environments at ambient and elevated temperatures has concentrated on crack propagation. Studies clearly reveal EIC involves two differentiable processes, one controlling initiation and the other propagation. Utilization of advanced high-resolution electron microscopy over the last 20 years has enabled more focused studies of crack initiation for stainless steel and nickel-based alloys at elevated temperatures exposed to environments associated with the nuclear industry. More recently, when coupled with advanced in-situ experimental techniques such as time-lapse X-ray computed 3D-tomography, progress has also been made for aluminum alloys suffering EIC at ambient temperatures. Conventional wisdom states that chemical processes are typically rate-controlling during EIC initiation. Additionally, experimental evidence based on primary creep exhaustion ahead of the introduction of an aggressive environment indicates that time-dependent mechanically-driven local microstructural strain accommodation processes (resembling creep-like behavior) often play an important role for many metals, even for temperatures as low as 40 % of their melting points (0.4 Tm). EIC studies reveal initial surface conditions and their associated immediate sub-surface alloy microstructures generated during creation (i.e. disturbed layers) can dictate whether or not EIC initiation occurs under mechanical loading conditions otherwise sufficient to enable initiation and growth. The plethora of quantitative experimental techniques now available to researchers should enable significant advances towards understanding EIC initiation.