The failure mechanism of field polyethylene gas pipeline with gas leakage at electrofusion joint

IF 2.3 4区 材料科学 Q2 METALLURGY & METALLURGICAL ENGINEERING Anti-corrosion Methods and Materials Pub Date : 2024-07-23 DOI:10.1108/acmm-04-2024-3000
Qing Bao, Baojin Wang, Manman Li, Chao Li, Jin Gao
{"title":"The failure mechanism of field polyethylene gas pipeline with gas leakage at electrofusion joint","authors":"Qing Bao, Baojin Wang, Manman Li, Chao Li, Jin Gao","doi":"10.1108/acmm-04-2024-3000","DOIUrl":null,"url":null,"abstract":"<h3>Purpose</h3>\n<p>A section of in-service PE gas pipeline in Guocun, Beijing, was found to appear gas leaking at the electrofusion (EF) joint. This study is dedicated to reveal the material cause of EF joint failure to help with a more accurate prediction of service life of PE gas pipe and further normalize the construction of PE gas pipeline.</p><!--/ Abstract__block -->\n<h3>Design/methodology/approach</h3>\n<p>Defect detection was carried out on the leaking EF joint using ultrasonic phased array. The mechanical degradation and structural aging behavior was studied by tension test, FTIR technology, TG test and DSC test. The organic components in the soil surrounding the PE gas pipe failure area were qualitatively identified.</p><!--/ Abstract__block -->\n<h3>Findings</h3>\n<p>The results showed that the organic surfactants in the soil environment could accelerate the aging behavior of PE material, leading to a deterioration of mechanical properties and a serious reduction in the ability of the PE pipe and EF joint, especially at the welding defect, to resist external force.</p><!--/ Abstract__block -->\n<h3>Originality/value</h3>\n<p>A novel study was conducted to investigate the failure cause of the EF joint of in-service PE gas pipe, incorporating the analysis of environmental factors and structural deterioration.</p><!--/ Abstract__block -->","PeriodicalId":8217,"journal":{"name":"Anti-corrosion Methods and Materials","volume":"19 1","pages":""},"PeriodicalIF":2.3000,"publicationDate":"2024-07-23","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Anti-corrosion Methods and Materials","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1108/acmm-04-2024-3000","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"METALLURGY & METALLURGICAL ENGINEERING","Score":null,"Total":0}
引用次数: 0

Abstract

Purpose

A section of in-service PE gas pipeline in Guocun, Beijing, was found to appear gas leaking at the electrofusion (EF) joint. This study is dedicated to reveal the material cause of EF joint failure to help with a more accurate prediction of service life of PE gas pipe and further normalize the construction of PE gas pipeline.

Design/methodology/approach

Defect detection was carried out on the leaking EF joint using ultrasonic phased array. The mechanical degradation and structural aging behavior was studied by tension test, FTIR technology, TG test and DSC test. The organic components in the soil surrounding the PE gas pipe failure area were qualitatively identified.

Findings

The results showed that the organic surfactants in the soil environment could accelerate the aging behavior of PE material, leading to a deterioration of mechanical properties and a serious reduction in the ability of the PE pipe and EF joint, especially at the welding defect, to resist external force.

Originality/value

A novel study was conducted to investigate the failure cause of the EF joint of in-service PE gas pipe, incorporating the analysis of environmental factors and structural deterioration.

查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
电熔接头处气体泄漏的现场聚乙烯燃气管道的失效机理
目的 在北京郭村的一段在役聚乙烯燃气管道上发现电熔(EF)接头处有气体泄漏。本研究致力于揭示电熔接头失效的材料原因,以帮助更准确地预测聚乙烯燃气管道的使用寿命,并进一步规范聚乙烯燃气管道的施工。通过拉伸试验、傅立叶变换红外技术、TG 试验和 DSC 试验研究了机械降解和结构老化行为。结果表明,土壤环境中的有机表面活性剂会加速聚乙烯材料的老化行为,导致聚乙烯管材和 EF 接头(尤其是焊接缺陷处)的机械性能恶化,抵抗外力的能力严重下降。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
Anti-corrosion Methods and Materials
Anti-corrosion Methods and Materials 工程技术-冶金工程
CiteScore
2.80
自引率
16.70%
发文量
61
审稿时长
13.5 months
期刊介绍: Anti-Corrosion Methods and Materials publishes a broad coverage of the materials and techniques employed in corrosion prevention. Coverage is essentially of a practical nature and designed to be of material benefit to those working in the field. Proven applications are covered together with company news and new product information. Anti-Corrosion Methods and Materials now also includes research articles that reflect the most interesting and strategically important research and development activities from around the world. Every year, industry pays a massive and rising cost for its corrosion problems. Research and development into new materials, processes and initiatives to combat this loss is increasing, and new findings are constantly coming to light which can help to beat corrosion problems throughout industry. This journal uniquely focuses on these exciting developments to make essential reading for anyone aiming to regain profits lost through corrosion difficulties. • New methods, materials and software • New developments in research and industry • Stainless steels • Protection of structural steelwork • Industry update, conference news, dates and events • Environmental issues • Health & safety, including EC regulations • Corrosion monitoring and plant health assessment • The latest equipment and processes • Corrosion cost and corrosion risk management.
期刊最新文献
Effect of graphene on mechanical and anti-corrosion properties of TiO2-SiO2 sol-gel coating Enhancing the corrosion resistance of a novel bio-compatible Mg-1Zn-0.45Ca alloy in simulated body fluid by a phosphate treated PEO coating A case study: anti-corrosion performances of plasma sprayed AT13 coatings on CrZrCu thin wall cylinder with adjusted parameters for controlling deformation A highly efficient method for characterizing the kinetics of hydrogen evolution reaction Research of two kinds of PANI@semiconductor based photocathodic coating corrosion protection effect and mechanism
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1