Co-Precipitation Synthesized Ag-Doped Ceria Redox Material (ACRM) for the Thermochemical Conversion of CO2 into Solar Fuels

Abstract

In this investigation, an effort was made to introduce Ag into the CeO2 fluorite crystal lattice to form Ce0.99Ag0.01O2-δ (ACRM) using an ammonium hydroxide-assisted co-precipitation method. The resulting powder obtained after the co-precipitation reaction, filtration, and drying was annealed at 800 °C in a muffle furnace to obtain crystalline ACRM. The phase composition and microstructure of the synthesized ACRM were analyzed using a powder X-ray diffractometer (PXRD) and a scanning electron microscope (SEM). The characterized ACRM powder was then subjected to multiple thermochemical thermal reduction (TR) and CO2 splitting (CDS) cycles using a high-temperature thermogravimetric analyzer (TGA). The TR step was conducted using Ar gas as an inert atmosphere, maintaining the temperature at 1400 °C for 60 min. Subsequently, the same powder was subjected to the CDS step by treating it with a gaseous mixture of 50% CO2 and Ar gas at 1000 °C for 30 min. ACRM displayed stable redox reactivity towards thermochemical CDS cycles by generating an average of 50.9 μmol of O2/g·cycle and 101.6 μmol of CO/g·cycle, respectively, over 10 thermochemical cycles.