Effect of Water on Wear of DLC Coatings in High Temperature and Pressurized Ethanol

IF 2.9 3区 工程技术 Q2 ENGINEERING, CHEMICAL Tribology Letters Pub Date : 2024-09-04 DOI:10.1007/s11249-024-01910-z
T. Tokoroyama, S. Horikawa, J. Mimata, N. Umehara, M. Murashima
{"title":"Effect of Water on Wear of DLC Coatings in High Temperature and Pressurized Ethanol","authors":"T. Tokoroyama,&nbsp;S. Horikawa,&nbsp;J. Mimata,&nbsp;N. Umehara,&nbsp;M. Murashima","doi":"10.1007/s11249-024-01910-z","DOIUrl":null,"url":null,"abstract":"<div><p>The friction and wear characteristics of a-C:H:Si and a-C:H coatings in an ethanol environment at 120 °C and 10 MPa focusing on the effects of water and dissolved oxygen in ethanol were investigated. The friction tests were conducted using an autoclave chamber, with gases (oxygen or nitrogen) and ethanol–water mixtures (0 and 6 vol.%). The wear acceleration of a-C:H:Si took place when it slid in ethanol with 6 vol.% water and pressurized by oxygen, thus the specific wear rate was the highest, approximately 1.8 × 10<sup>−7</sup> mm<sup>3</sup>/Nm. The reason of this wear acceleration was assumed the effect of hardness reduction due to oxidation of the a-C:H:Si, so the O/C ratio by AES and the hardness of topmost surface by AFM nano-scratch were investigated. As a result, the higher O/C ratio showed higher specific wear rate due to the hardness reduction from 13.3 to 6.0 GPa. These findings highlight the role of water and dissolved oxygen in accelerating wear of a-C:H:Si coatings.</p><h3>Graphical abstract</h3>\n<div><figure><div><div><picture><source><img></source></picture></div></div></figure></div></div>","PeriodicalId":806,"journal":{"name":"Tribology Letters","volume":null,"pages":null},"PeriodicalIF":2.9000,"publicationDate":"2024-09-04","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://link.springer.com/content/pdf/10.1007/s11249-024-01910-z.pdf","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Tribology Letters","FirstCategoryId":"5","ListUrlMain":"https://link.springer.com/article/10.1007/s11249-024-01910-z","RegionNum":3,"RegionCategory":"工程技术","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"ENGINEERING, CHEMICAL","Score":null,"Total":0}
引用次数: 0

Abstract

The friction and wear characteristics of a-C:H:Si and a-C:H coatings in an ethanol environment at 120 °C and 10 MPa focusing on the effects of water and dissolved oxygen in ethanol were investigated. The friction tests were conducted using an autoclave chamber, with gases (oxygen or nitrogen) and ethanol–water mixtures (0 and 6 vol.%). The wear acceleration of a-C:H:Si took place when it slid in ethanol with 6 vol.% water and pressurized by oxygen, thus the specific wear rate was the highest, approximately 1.8 × 10−7 mm3/Nm. The reason of this wear acceleration was assumed the effect of hardness reduction due to oxidation of the a-C:H:Si, so the O/C ratio by AES and the hardness of topmost surface by AFM nano-scratch were investigated. As a result, the higher O/C ratio showed higher specific wear rate due to the hardness reduction from 13.3 to 6.0 GPa. These findings highlight the role of water and dissolved oxygen in accelerating wear of a-C:H:Si coatings.

Graphical abstract

Abstract Image

查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
水在高温和加压乙醇中对 DLC 涂层磨损的影响
研究了 a-C:H:Si 和 a-C:H 涂层在 120 °C 和 10 MPa 的乙醇环境中的摩擦和磨损特性,重点研究了乙醇中水和溶解氧的影响。摩擦试验是在高压灭菌室、气体(氧气或氮气)和乙醇-水混合物(0 和 6 vol.%)中进行的。当 a-C:H:Si 在含 6 Vol.% 水的乙醇中滑动并受到氧气加压时,磨损加速,因此比磨损率最高,约为 1.8 × 10-7 mm3/Nm。磨损加速的原因被认为是 a-C:H:Si 氧化导致硬度降低的影响,因此研究了 AES 的 O/C 比和 AFM 纳米划痕的最顶层表面硬度。结果表明,由于硬度从 13.3 GPa 降至 6.0 GPa,O/C 比越高,比磨损率越高。这些发现突出了水和溶解氧在加速 a-C:H:Si 涂层磨损中的作用。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
Tribology Letters
Tribology Letters 工程技术-工程:化工
CiteScore
5.30
自引率
9.40%
发文量
116
审稿时长
2.5 months
期刊介绍: Tribology Letters is devoted to the development of the science of tribology and its applications, particularly focusing on publishing high-quality papers at the forefront of tribological science and that address the fundamentals of friction, lubrication, wear, or adhesion. The journal facilitates communication and exchange of seminal ideas among thousands of practitioners who are engaged worldwide in the pursuit of tribology-based science and technology.
期刊最新文献
Wear Mechanism and Wear Debris Characterization of ULWPE in Multidirectional Motion Cobalt- and Chromium-Oxide-Based Coatings: Thermally Spraying a Glaze Layer Visualization of Structural Deformation of Polymer Additives in Oil Under High Shear Flow Influence of Variable-Depth Groove Texture on the Friction and Wear Performance of GCr15–SiC Friction Pairs Under Water Lubrication The Flow of Lubricant as a Mist in the Piston Assembly and Crankcase of a Fired Gasoline Engine: The Effect of Viscosity Modifier and the Link to Lubricant Degradation
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1