Huizi Liu , Changzeng Fan , Bin Wen , Lifeng Zhang
{"title":"Titanium vanadium nickel, TiV0.08Ni0.92","authors":"Huizi Liu , Changzeng Fan , Bin Wen , Lifeng Zhang","doi":"10.1107/S2414314625001476","DOIUrl":null,"url":null,"abstract":"<div><div>A single-crystal of the intermetallic phase TiV<sub>0.08</sub>Ni<sub>0.92</sub> was obtained by the high-temperature sintering of a mixture of nominal composition Ti<sub>0.9</sub>V<sub>0.1</sub>Ni. The title compound adopts the CsCl structure type with one site solely occupied by Ti and the other by V and Ni with a ratio of 0.08 (7):0.92 (7).</div></div><div><div>A single-crystal of the intermetallic phase TiV<sub>0.08</sub>Ni<sub>0.92</sub> was obtained by the high-temperature sintering of a mixture of nominal composition Ti<sub>0.9</sub>V<sub>0.1</sub>Ni. The title compound adopts the CsCl structure type with one site solely occupied by Ti and the other by V and Ni with a ratio of 0.08 (7):0.92 (7).<span><figure><span><img><ol><li><span><span>Download: <span>Download high-res image (97KB)</span></span></span></li><li><span><span>Download: <span>Download full-size image</span></span></span></li></ol></span></figure></span></div></div>","PeriodicalId":94324,"journal":{"name":"IUCrData","volume":"10 2","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2025-02-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.ncbi.nlm.nih.gov/pmc/articles/PMC11904629/pdf/","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"IUCrData","FirstCategoryId":"1085","ListUrlMain":"https://www.sciencedirect.com/org/science/article/pii/S2414314625000148","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"2025/2/25 0:00:00","PubModel":"Epub","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
A single-crystal of the intermetallic phase TiV0.08Ni0.92 was obtained by the high-temperature sintering of a mixture of nominal composition Ti0.9V0.1Ni. The title compound adopts the CsCl structure type with one site solely occupied by Ti and the other by V and Ni with a ratio of 0.08 (7):0.92 (7).
A single-crystal of the intermetallic phase TiV0.08Ni0.92 was obtained by the high-temperature sintering of a mixture of nominal composition Ti0.9V0.1Ni. The title compound adopts the CsCl structure type with one site solely occupied by Ti and the other by V and Ni with a ratio of 0.08 (7):0.92 (7).
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们