IN VITRO SURVIVAL AND FRACTURE FORCE OF LITHIUM DISILICATE HYBRID ABUTMENT CROWNS.

IF 1.8 The International journal of prosthodontics Pub Date : 2024-09-27 DOI:10.11607/ijp.8548

Tobias Graf, Elisabeth Völler, Josef Schweiger, Michael Stimmelmayr, Jan-Frederik Güth, Kurt-Jürgen Erdelt

{"title":"IN VITRO SURVIVAL AND FRACTURE FORCE OF LITHIUM DISILICATE HYBRID ABUTMENT CROWNS.","authors":"Tobias Graf, Elisabeth Völler, Josef Schweiger, Michael Stimmelmayr, Jan-Frederik Güth, Kurt-Jürgen Erdelt","doi":"10.11607/ijp.8548","DOIUrl":null,"url":null,"abstract":"Purpose: To evaluate the behavior of hybrid abutment crowns fabricated from monolithic lithium disilicate ceramic (LDC) and to compare the influence of different in vitro artificial aging protocols.Materials and methods: A total of 32 monolithic hybrid abutment crowns of monolithic LDC were fabricated. Of these, 24 were artificially aged using three different protocols up to a 20 year simulation (1.2 × 106, 2.4 × 106, 4.8 × 106 chewing cycles, thermocycling), a control group underwent no artificial aging (n = 8, N = 32). Load-to-failure tests were conducted for all specimens, and failure values were compared (P < .05).Results: All specimens passed in vitro aging. Mean failure load values between 532.6 and 562.8 N were found but did neither differ significantly among the test groups nor from the control group.Conclusions: Within the limitations of this in vitro pilot study, hybrid abutment crowns manufactured from monolithic LDC seem to offer appropriate long-lasting mechanical stability over a simulation period up to 20 years. The failure values and complication pattern seem to be independent of several aging protocols in this test set-up.","PeriodicalId":94232,"journal":{"name":"The International journal of prosthodontics","volume":"0 0","pages":"223-227"},"PeriodicalIF":1.8000,"publicationDate":"2024-09-27","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"The International journal of prosthodontics","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.11607/ijp.8548","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}

引用次数: 0

Abstract

Purpose: To evaluate the behavior of hybrid abutment crowns fabricated from monolithic lithium disilicate ceramic (LDC) and to compare the influence of different in vitro artificial aging protocols.

Materials and methods: A total of 32 monolithic hybrid abutment crowns of monolithic LDC were fabricated. Of these, 24 were artificially aged using three different protocols up to a 20 year simulation (1.2 × 106, 2.4 × 106, 4.8 × 106 chewing cycles, thermocycling), a control group underwent no artificial aging (n = 8, N = 32). Load-to-failure tests were conducted for all specimens, and failure values were compared (P < .05).

Results: All specimens passed in vitro aging. Mean failure load values between 532.6 and 562.8 N were found but did neither differ significantly among the test groups nor from the control group.

Conclusions: Within the limitations of this in vitro pilot study, hybrid abutment crowns manufactured from monolithic LDC seem to offer appropriate long-lasting mechanical stability over a simulation period up to 20 years. The failure values and complication pattern seem to be independent of several aging protocols in this test set-up.

查看原文

微信好友朋友圈 QQ好友复制链接

本刊更多论文

二硅酸锂复合基台牙冠的体外存活和断裂力。

目的：评价由单片二硅酸锂陶瓷（LDC）制成的混合基牙牙冠的性能，并比较不同体外人工老化方案的影响。材料与方法：制作了32个单块LDC单块混合基牙冠。24人采用3种不同的方案进行人工老化，直至20年模拟（1.2×106、2.4×106、4.8×106咀嚼周期、热循环），一个对照组未进行人工老化（N=32，N=8）。对所有试样进行了荷载-破坏试验，并对破坏值进行了比较（p结果/结论：所有样本都通过了体外老化。平均失效载荷值在532.6和562.8 N之间，但试验组和对照组之间没有显著差异。在这项体外试验研究的限制范围内，由单片LDC制造的混合基牙牙冠似乎比模拟iod长达20年。在该测试设置中，故障值和并发症模式似乎与几个老化协议无关。