Effect of Ce Addition on Adsorption and Oxidation of NO over MnO x /Al2O3

Abstract

The MnO x /Al2O3 catalysts with different Ce content doping were prepared by an ultrasonic impregnation method, and the catalytic activity for NO oxidation removal was tested in a fixed-bed quartz tube furnace. Simultaneously, the catalysts were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), full-automatic physical-chemical adsorption instrument, and field emission scanning electron microscope (FESEM) to analyze the effect of Ce addition on the adsorption capacity and catalytic activity. Experimental results validated that the activity of the MnO x /Al2O3 catalyst was greatly promoted with Ce addition. According to the characterization results, it could be concluded that Ce doping led to significant changes in the crystalline phase on the catalyst surface, which increased the relative content of surface lattice oxygen and promoted the catalytic oxidation of NO. By observing the physical properties of the surface and analyzing the surface elements of the catalyst, it could be inferred that a manganese-cerium solid solution was formed on the surface of Mn0.4Ce0.05/Al. Moreover, Ce addition increased the catalyst pore size, which enhanced the adsorption and contact of NO and O2 with the active sites on the catalyst surface, and reduced the resistance of the reactants during internal diffusion. All these variations assigned to Mn0.4Ce0.05/Al were favorable for the catalytic oxidation of NO.