Effects of organic modified hectorite on performance, isothermal crystallization behavior and interface interaction of poly(lactic acid) film

IF 5.3 2区 地球科学 Q2 CHEMISTRY, PHYSICAL Applied Clay Science Pub Date : 2023-11-01 DOI:10.1016/j.clay.2023.107118
Yikelamu Jilili, Yumiao Ma, Zhe Wang, Weijun Zhen
{"title":"Effects of organic modified hectorite on performance, isothermal crystallization behavior and interface interaction of poly(lactic acid) film","authors":"Yikelamu Jilili,&nbsp;Yumiao Ma,&nbsp;Zhe Wang,&nbsp;Weijun Zhen","doi":"10.1016/j.clay.2023.107118","DOIUrl":null,"url":null,"abstract":"<div><p><span><span>In this work, in order to improve the properties of PLA, Hec-g@OA/PLA nanocomposite<span> films were prepared by a single-screw extrusion film blown machine with PLA as a matrix and organically modified </span></span>hectorite (Hec-g@OA) as a filler, and the optimum filler mass ratio of Hec-g@OA was preferred as an objective function of mechanical properties. The mechanical properties of PLA were found to increase from 24.31% to 61.75% when the mass percentage of Hec-g@OA was 0.3 wt%. Secondly, </span>isothermal<span> crystallization behavior of the nanocomposite films was analyzed by simultaneous rheology and FTIR technology for the purpose of further studied the effect of Hec-g@OA on the isothermal crystallization behavior of PLA, which showed that the half-crystallization time of Hec-g@OA/PLA decreased from 7.01 min, 28.99 min and 77.88 min to 3.87 min, 20.59 min and 65.78 min, respectively, at 130 °C, 135 °C and 140 °C. Finally, the form of the interaction between PLA and Hec-g@OA was analysis by electronic structure calculations and energy decomposition, it was analyzed that electrostatic interaction was found to be the main impact factor for induced crystallization of Hec-g@OA/PLA nanocomposite films, while induction and dispersion were found to be the minor impact factors.</span></p></div>","PeriodicalId":245,"journal":{"name":"Applied Clay Science","volume":"244 ","pages":"Article 107118"},"PeriodicalIF":5.3000,"publicationDate":"2023-11-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Applied Clay Science","FirstCategoryId":"89","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0169131723003058","RegionNum":2,"RegionCategory":"地球科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"CHEMISTRY, PHYSICAL","Score":null,"Total":0}
引用次数: 0

Abstract

In this work, in order to improve the properties of PLA, Hec-g@OA/PLA nanocomposite films were prepared by a single-screw extrusion film blown machine with PLA as a matrix and organically modified hectorite (Hec-g@OA) as a filler, and the optimum filler mass ratio of Hec-g@OA was preferred as an objective function of mechanical properties. The mechanical properties of PLA were found to increase from 24.31% to 61.75% when the mass percentage of Hec-g@OA was 0.3 wt%. Secondly, isothermal crystallization behavior of the nanocomposite films was analyzed by simultaneous rheology and FTIR technology for the purpose of further studied the effect of Hec-g@OA on the isothermal crystallization behavior of PLA, which showed that the half-crystallization time of Hec-g@OA/PLA decreased from 7.01 min, 28.99 min and 77.88 min to 3.87 min, 20.59 min and 65.78 min, respectively, at 130 °C, 135 °C and 140 °C. Finally, the form of the interaction between PLA and Hec-g@OA was analysis by electronic structure calculations and energy decomposition, it was analyzed that electrostatic interaction was found to be the main impact factor for induced crystallization of Hec-g@OA/PLA nanocomposite films, while induction and dispersion were found to be the minor impact factors.

Abstract Image

查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
有机改性锂云母对聚乳酸膜性能、等温结晶行为及界面相互作用的影响
为了提高聚乳酸的性能,采用单螺杆挤出吹膜机,以聚乳酸为基体,有机改性赫托石(Hec-g@OA)为填料制备了Hec-g@OA/PLA纳米复合薄膜,并优选了最佳填料质量比Hec-g@OA作为力学性能的目标函数。当Hec-g@OA质量百分比为0.3 wt%时,PLA的力学性能从24.31%提高到61.75%。其次,通过同时流变学和FTIR技术分析纳米复合膜的等温结晶行为,进一步研究Hec-g@OA对PLA等温结晶行为的影响。结果表明,在130℃、135℃和140℃下,Hec-g@OA/PLA的半结晶时间分别从7.01 min、28.99 min和77.88 min降低到3.87 min、20.59 min和65.78 min。最后,通过电子结构计算和能量分解分析了PLA与Hec-g@OA的相互作用形式,发现静电相互作用是Hec-g@OA/PLA纳米复合膜诱导结晶的主要影响因素,而诱导和分散是次要影响因素。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
Applied Clay Science
Applied Clay Science 地学-矿物学
CiteScore
10.30
自引率
10.70%
发文量
289
审稿时长
39 days
期刊介绍: Applied Clay Science aims to be an international journal attracting high quality scientific papers on clays and clay minerals, including research papers, reviews, and technical notes. The journal covers typical subjects of Fundamental and Applied Clay Science such as: • Synthesis and purification • Structural, crystallographic and mineralogical properties of clays and clay minerals • Thermal properties of clays and clay minerals • Physico-chemical properties including i) surface and interface properties; ii) thermodynamic properties; iii) mechanical properties • Interaction with water, with polar and apolar molecules • Colloidal properties and rheology • Adsorption, Intercalation, Ionic exchange • Genesis and deposits of clay minerals • Geology and geochemistry of clays • Modification of clays and clay minerals properties by thermal and physical treatments • Modification by chemical treatments with organic and inorganic molecules(organoclays, pillared clays) • Modification by biological microorganisms. etc...
期刊最新文献
Editorial Board Synthesis of phosphonitrile derivative-modified halloysite flame retardants and their simultaneous enhancement of epoxy resins flame retardancy and mechanical properties Hysteresis at low humidity on vapor sorption isotherm of Ca-montmorillonite: The key role of interlayer cations Cronstedtite: H2 generation and new constraints on its formation conditions Tea nanoparticles modified halloysite clay coated polyurethane sponge as multifunctional sensors
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1