Effect of heat treatment parameters on microstructure, defects, and properties of Al-16Si-6Cu automotive shift fork: quantitative evaluation perspective
{"title":"Effect of heat treatment parameters on microstructure, defects, and properties of Al-16Si-6Cu automotive shift fork: quantitative evaluation perspective","authors":"Saeed Farahany, Mustafa Abazari","doi":"10.1080/13640461.2022.2082758","DOIUrl":null,"url":null,"abstract":"ABSTRACT The current study investigated the effect of heat treatment parameters, including solution treatment temperature (STT), time, and quench rate, on the microstructure, defects, and hardness of an Al-16Si-6Cu Shift fork die-cast alloy. The changes in primary silicon particle (PSP) features were examined quantitatively by optical microscopy, coupled with image analysis and SEM equipped with EDS. The biggest PSPs (27 ± 8 µm) and the highest area fraction (23%) were found in the sample solution treated at 470°C and cooled in the furnace. The hardness value increased in heat-treated samples slightly (140–148 BHN). A lower STT (420°C) and a lower ageing time (1 h) are suitable conditions for the heat treatment of an Al-16Si-6Cu die-cast alloy, in which a lower pore area fraction, 1.18, smaller pore, 4.5 μm, along with finer primary silicon, 9.5 ± 3 μm, with higher circularity, 0.38 ± 0.04, was achieved.","PeriodicalId":13939,"journal":{"name":"International Journal of Cast Metals Research","volume":null,"pages":null},"PeriodicalIF":1.3000,"publicationDate":"2022-05-04","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"International Journal of Cast Metals Research","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1080/13640461.2022.2082758","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"METALLURGY & METALLURGICAL ENGINEERING","Score":null,"Total":0}
引用次数: 0
Abstract
ABSTRACT The current study investigated the effect of heat treatment parameters, including solution treatment temperature (STT), time, and quench rate, on the microstructure, defects, and hardness of an Al-16Si-6Cu Shift fork die-cast alloy. The changes in primary silicon particle (PSP) features were examined quantitatively by optical microscopy, coupled with image analysis and SEM equipped with EDS. The biggest PSPs (27 ± 8 µm) and the highest area fraction (23%) were found in the sample solution treated at 470°C and cooled in the furnace. The hardness value increased in heat-treated samples slightly (140–148 BHN). A lower STT (420°C) and a lower ageing time (1 h) are suitable conditions for the heat treatment of an Al-16Si-6Cu die-cast alloy, in which a lower pore area fraction, 1.18, smaller pore, 4.5 μm, along with finer primary silicon, 9.5 ± 3 μm, with higher circularity, 0.38 ± 0.04, was achieved.
期刊介绍：
The International Journal of Cast Metals Research is devoted to the dissemination of peer reviewed information on the science and engineering of cast metals, solidification and casting processes. Assured production of high integrity castings requires an integrated approach that optimises casting, mould and gating design; mould materials and binders; alloy composition and microstructure; metal melting, modification and handling; dimensional control; and finishing and post-treatment of the casting. The Journal reports advances in both the fundamental science and materials and production engineering contributing to the successful manufacture of fit for purpose castings.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们