Microstructural Evolution and Room Temperature Mechanical Properties in Additively Manufactured Mar M 509 with Short Cycle Heat Treatment.

IF 1.5 4区 材料科学 Q3 ENGINEERING, MECHANICAL Journal of Engineering Materials and Technology-transactions of The Asme Pub Date : 2023-08-25 DOI:10.1115/1.4063257
Shreehard Sahu, B. Kumar, S. Sahoo, Nagamani Jaya Balila, D. Srinivasan
{"title":"Microstructural Evolution and Room Temperature Mechanical Properties in Additively Manufactured Mar M 509 with Short Cycle Heat Treatment.","authors":"Shreehard Sahu, B. Kumar, S. Sahoo, Nagamani Jaya Balila, D. Srinivasan","doi":"10.1115/1.4063257","DOIUrl":null,"url":null,"abstract":"\n The Co-based superalloy Mar M 509, known for its high-temperature oxidation and hot corrosion resistance, is processed via laser powder bed fusion (LPBF). Microstructure and mechanical properties of Mar M 509 in as-printed (As-P) and heat-treated (HT) states are compared based on two build orientations (longitudinal (L) and transverse (T)) to establish structure-property links with heat treatment. The As-P condition displays a distinct cellular microstructure (500-600 nm) with 50-60 nm carbide particles adorning cell boundaries. Longitudinal (L) build has columnar grains (8-35 μm along major axis) with a grain aspect ratio of 4, while transverse (T) orientation exhibits equiaxed, bimodal microstructure (5-10 μm and 15-25 μm grain sizes). Strong <001> texture is noted in L. Mechanical properties at room temperature differ between L and T; T (569±12HV) has 15% higher hardness compared to L (489±18HV) and 34% higher 0.2% yield strength (YS), but 30% lower elongation than L. Post a short heat treatment cycle at 1250°C, weld bead structure and cell boundaries break down. Both L (25-33 μm along major axis) and T orientations (5-42 μm) experience grain growth, and carbides coarsen (250-350 nm). Post-heat treatment, dislocation density decreases, indicating recrystallization; lattice parameter of matrix reduces, implying solute depletion contributing to carbide enrichment. Yield strength drops from 860 MPa to 740 MPa in L and from 1150 MPa to 840 MPa in T, with ductility rising from 14% to 23% in L.","PeriodicalId":15700,"journal":{"name":"Journal of Engineering Materials and Technology-transactions of The Asme","volume":null,"pages":null},"PeriodicalIF":1.5000,"publicationDate":"2023-08-25","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Engineering Materials and Technology-transactions of The Asme","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1115/1.4063257","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"ENGINEERING, MECHANICAL","Score":null,"Total":0}
引用次数: 0

Abstract

The Co-based superalloy Mar M 509, known for its high-temperature oxidation and hot corrosion resistance, is processed via laser powder bed fusion (LPBF). Microstructure and mechanical properties of Mar M 509 in as-printed (As-P) and heat-treated (HT) states are compared based on two build orientations (longitudinal (L) and transverse (T)) to establish structure-property links with heat treatment. The As-P condition displays a distinct cellular microstructure (500-600 nm) with 50-60 nm carbide particles adorning cell boundaries. Longitudinal (L) build has columnar grains (8-35 μm along major axis) with a grain aspect ratio of 4, while transverse (T) orientation exhibits equiaxed, bimodal microstructure (5-10 μm and 15-25 μm grain sizes). Strong <001> texture is noted in L. Mechanical properties at room temperature differ between L and T; T (569±12HV) has 15% higher hardness compared to L (489±18HV) and 34% higher 0.2% yield strength (YS), but 30% lower elongation than L. Post a short heat treatment cycle at 1250°C, weld bead structure and cell boundaries break down. Both L (25-33 μm along major axis) and T orientations (5-42 μm) experience grain growth, and carbides coarsen (250-350 nm). Post-heat treatment, dislocation density decreases, indicating recrystallization; lattice parameter of matrix reduces, implying solute depletion contributing to carbide enrichment. Yield strength drops from 860 MPa to 740 MPa in L and from 1150 MPa to 840 MPa in T, with ductility rising from 14% to 23% in L.
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Mar M 509短周期热处理后的组织演变和室温力学性能。
钴基高温合金Mar M 509以其耐高温氧化和热腐蚀性而闻名,它是通过激光粉末床熔融(LPBF)处理的。基于两个构建方向(纵向(L)和横向(T)),比较了Mar M 509在印刷态(as-P)和热处理态(HT)下的微观结构和力学性能,以建立与热处理的结构-性能联系。As-P条件显示出明显的细胞微结构(500-600nm),其中50-60nm的碳化物颗粒装饰细胞边界。纵向(L)结构具有晶粒纵横比为4的柱状晶粒(沿主轴8-35μm),而横向(T)取向表现出等轴双峰微观结构(5-10μm和15-25μm晶粒尺寸)。L具有强烈的织构。室温下L和T的机械性能不同;与L(489±18HV)相比,T(569±12HV)的硬度高出15%,屈服强度(YS)高出34%,但伸长率比L低30%。在1250°C的短热处理循环后,焊道结构和细胞边界破裂。L(沿主轴25-33μm)和T取向(5-42μm)都经历晶粒生长,碳化物粗化(250-350 nm)。热处理后,位错密度降低,表明再结晶;基体晶格参数降低,表明溶质贫化有助于碳化物富集。屈服强度从L的860MPa下降到740MPa,从T的1150MPa下降到840MPa,延展性从L的14%上升到23%。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
CiteScore
3.00
自引率
0.00%
发文量
30
审稿时长
4.5 months
期刊介绍: Multiscale characterization, modeling, and experiments; High-temperature creep, fatigue, and fracture; Elastic-plastic behavior; Environmental effects on material response, constitutive relations, materials processing, and microstructure mechanical property relationships
期刊最新文献
Effect of Build Geometry and Porosity in Additively Manufactured CuCrZr Influence of Multiple Modifications on the Fatigue Behavior of Bitumen and Asphalt Mixtures High Temperature Tensile and Compressive Behaviors of Nanostructured Polycrystalline AlCoCrFeNi High Entropy Alloy: A Molecular Dynamics Study Simulation of Pitting Corrosion Under Stress Based on Cellular Automata and Finite Element Method Corrosion Behavior of 20G Steel in Saline (Na2SO4) Circumstances at High Temperature/Pressure
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1