Synthesis of SAPO-34 catalysts via sonochemically prepared method and its catalytic performance in methanol conversion to light olefins

Abstract

Methanol-to-olefin (MTO) reaction was investigated over sonochemically (SAPO-34-U40, SAPO-34-U70, SAPO-34-U100) and hydrothermally (SAPO-34-HT) prepared nanocatalysts. The catalytic performance of prepared samples was investigated over all samples at 450?°C and over SAPO-34-U40 at 350–450?°C temperature range. The higher yield ~?97?wt% (31.4?wt% C₂₌, 49.4?wt% C₃₌ and 16.1?wt% sumC₄₌) of light olefins was obtained at 375?°C on SAPO-34-U40. Physico-chemical properties of catalysts were characterized by XRD, SEM, BET, ICP techniques. XRD analysis showed suitable crystalline structure and SEM images confirmed perfect crystallinity of sonochemically prepared samples. BET analysis indicated remarkable surface area of SAPO-34-U40. The amount of carbon deposits and character of coke was determined by TPO analysis. The higher amount of coke was determined over SAPO-34-HT in comparison to another’s at 450?°C. The character of coke deposited over SAPO-34-U40 was similar for 375–425?°C temperatures.