Research on the Performance of Polypyrrole Coated Conductive Fabrics Prepared from Different Base Materials

IF 0.7 4区 工程技术 Q3 MATERIALS SCIENCE, TEXTILES Fibres & Textiles in Eastern Europe Pub Date : 2023-07-01 DOI:10.2478/ftee-2023-0018
Yuanjun Liu, Huangyu Xue, Yanyan Liu, Jiaqi Zhao, Haiying Wu, Xiaoming Zhao
{"title":"Research on the Performance of Polypyrrole Coated Conductive Fabrics Prepared from Different Base Materials","authors":"Yuanjun Liu, Huangyu Xue, Yanyan Liu, Jiaqi Zhao, Haiying Wu, Xiaoming Zhao","doi":"10.2478/ftee-2023-0018","DOIUrl":null,"url":null,"abstract":"Abstract In this paper, polypyrrole coated conductive fabrics were prepared using pyrrole as the monomer, p-toluene sulfonic acid as the doping agent and ammonium persulfate as the oxidant, adopting the simple method of situ polymerization of the liquid phase. Six types of conductive polypyrrole coated fabrics were prepared adopting polyester-cotton blended fabrics, nylon fabrics, wool fabrics, silk fabrics, basalt fabrics and aramid fabric respectively as base materials and using the same process conditions; its electrical conductivity was compared, and the distribution and resistance of the washing fastness of polypyrrole on the surface of those fabrics were studied. Results showed that under the same process conditions, the conductivity of polypyrrole coated terylene fabrics was the best, followed by the polypyrrole coated nylon fabrics and polypyrrole coated wool fabrics. Observed by electron microscope, the distribution of polypyrrole was more homogeneous on different base cloths. After washing, it was concluded that the combination fastness of polypyrrole with polyester-cotton, nylon and wool was better, while the combination fastness of polypyrrole with basalt and aramid was poor.","PeriodicalId":12309,"journal":{"name":"Fibres & Textiles in Eastern Europe","volume":"31 1","pages":"75 - 81"},"PeriodicalIF":0.7000,"publicationDate":"2023-07-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Fibres & Textiles in Eastern Europe","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.2478/ftee-2023-0018","RegionNum":4,"RegionCategory":"工程技术","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"MATERIALS SCIENCE, TEXTILES","Score":null,"Total":0}
引用次数: 0

Abstract

Abstract In this paper, polypyrrole coated conductive fabrics were prepared using pyrrole as the monomer, p-toluene sulfonic acid as the doping agent and ammonium persulfate as the oxidant, adopting the simple method of situ polymerization of the liquid phase. Six types of conductive polypyrrole coated fabrics were prepared adopting polyester-cotton blended fabrics, nylon fabrics, wool fabrics, silk fabrics, basalt fabrics and aramid fabric respectively as base materials and using the same process conditions; its electrical conductivity was compared, and the distribution and resistance of the washing fastness of polypyrrole on the surface of those fabrics were studied. Results showed that under the same process conditions, the conductivity of polypyrrole coated terylene fabrics was the best, followed by the polypyrrole coated nylon fabrics and polypyrrole coated wool fabrics. Observed by electron microscope, the distribution of polypyrrole was more homogeneous on different base cloths. After washing, it was concluded that the combination fastness of polypyrrole with polyester-cotton, nylon and wool was better, while the combination fastness of polypyrrole with basalt and aramid was poor.
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
不同基材制备聚吡咯涂层导电织物性能的研究
摘要本文以吡咯为单体,对甲苯磺酸为掺杂剂,过硫酸铵为氧化剂,采用简单的液相原位聚合法制备了聚吡咯涂层导电织物。以涤棉混纺织物、尼龙织物、羊毛织物、真丝织物、玄武岩织物和芳纶织物为基料,在相同的工艺条件下,分别制备了6种导电聚吡咯涂层织物;比较了其电导率,研究了聚吡咯在织物表面的分布和耐洗涤牢度。结果表明,在相同的工艺条件下,聚吡咯涂层涤纶织物的导电性能最好,其次是聚吡咯涂层尼龙织物和聚吡咯涂层羊毛织物。电镜观察发现,聚吡咯在不同基布上的分布较为均匀。洗涤后得出聚吡咯与涤棉、尼龙、羊毛的结合牢度较好,而与玄武岩、芳纶的结合牢度较差。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
Fibres & Textiles in Eastern Europe
Fibres & Textiles in Eastern Europe 工程技术-材料科学:纺织
CiteScore
1.60
自引率
11.10%
发文量
12
审稿时长
13.5 months
期刊介绍: FIBRES & TEXTILES in Eastern Europe is a peer reviewed bimonthly scientific journal devoted to current problems of fibre, textile and fibrous products’ science as well as general economic problems of textile industry worldwide. The content of the journal is available online as free open access. FIBRES & TEXTILES in Eastern Europe constitutes a forum for the exchange of information and the establishment of mutual contact for cooperation between scientific centres, as well as between science and industry.
期刊最新文献
Investigation of the Accelerated Ageing of Carbon-Epoxy Composites on their Mechanical Properties Knitted Heating Mats Evaluation of Insulation against Contact Heat, Radiant Heat and Sensory Comfort of Basalt Fabric-Based Composites with Parylene C Coating Digital Inheritance of Traditional Mongolian Robes of the Nayman Tribe Experimental Investigation on the Bending Behavior of Weft Interlaced Multilayered Woven Fabrics for Composite Applications
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1