{"title":"On the nanoindentation behavior of a TiC layer formed through thermo-reactive diffusion during hot pressing of Ti and cast iron","authors":"Marius Grad , Naresh Nadammal , Darius Tytko , Ulf Noster","doi":"10.1016/j.mlblux.2022.100161","DOIUrl":null,"url":null,"abstract":"<div><p>Hot pressing of pure Ti and cast iron under vacuum formed a ∼15 µm wide TiC-layer through the thermo-reactive diffusion process. Nanoindentation testing of the TiC-layer revealed average hardness and elastic modulus values of ∼35 GPa and ∼400 GPa, respectively. High-resolution indentation mapping indicated hardness change across the boundary with peak values observed within the TiC-layer. Solid state high temperature diffusion holds significant potential for developing uniform hard coatings on pure Ti/Ti-alloys.</p></div>","PeriodicalId":18245,"journal":{"name":"Materials Letters: X","volume":"15 ","pages":"Article 100161"},"PeriodicalIF":2.2000,"publicationDate":"2022-09-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.sciencedirect.com/science/article/pii/S2590150822000412/pdfft?md5=02c95108987e5b04bb6d90f277355a3d&pid=1-s2.0-S2590150822000412-main.pdf","citationCount":"1","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Letters: X","FirstCategoryId":"1085","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S2590150822000412","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 1
Abstract
Hot pressing of pure Ti and cast iron under vacuum formed a ∼15 µm wide TiC-layer through the thermo-reactive diffusion process. Nanoindentation testing of the TiC-layer revealed average hardness and elastic modulus values of ∼35 GPa and ∼400 GPa, respectively. High-resolution indentation mapping indicated hardness change across the boundary with peak values observed within the TiC-layer. Solid state high temperature diffusion holds significant potential for developing uniform hard coatings on pure Ti/Ti-alloys.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们