{"title":"Novel Nb5+-doped hexagonal perovskite Ba5In2Al2ZrO13 (structure, hydration, electrical conductivity)","authors":"R. Andreev, D. Korona, I. Anokhina, I. Animitsa","doi":"10.15826/chimtech.2022.9.4.14","DOIUrl":null,"url":null,"abstract":"The new phase Ba5In2Al2Zr0.9Nb0.1O13.05 with hexagonal perovskite structure was obtained. The substitution of Zr4+ by smaller Nb5+ was accompanied by the incorporation of the oxygen interstitials and did not lead to a significant change in the lattice parameters. It was established that the investigated sample was capable for water incorporation from the gas phase, the hydration degree value was 0.24 mol H2O. IR-spectroscopy analysis defined the presence of OH−-groups with different thermal stability, which participate in different hydrogen bonds. The new phase Ba5In2Al2Zr0.9Nb0.1O13.05 demonstrates the predominant protonic conductivity at pH2O = 2·10−2 atm and Т600 °C.","PeriodicalId":9964,"journal":{"name":"Chimica Techno Acta","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2022-10-10","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"3","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Chimica Techno Acta","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.15826/chimtech.2022.9.4.14","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"Materials Science","Score":null,"Total":0}
引用次数: 3
Abstract
The new phase Ba5In2Al2Zr0.9Nb0.1O13.05 with hexagonal perovskite structure was obtained. The substitution of Zr4+ by smaller Nb5+ was accompanied by the incorporation of the oxygen interstitials and did not lead to a significant change in the lattice parameters. It was established that the investigated sample was capable for water incorporation from the gas phase, the hydration degree value was 0.24 mol H2O. IR-spectroscopy analysis defined the presence of OH−-groups with different thermal stability, which participate in different hydrogen bonds. The new phase Ba5In2Al2Zr0.9Nb0.1O13.05 demonstrates the predominant protonic conductivity at pH2O = 2·10−2 atm and Т600 °C.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们