{"title":"CHARACTERISTICS OF PHYSICAL PROPERTIES OF WOOD POWDER COMPOSITES AND BAGASSEAS CONSTRUCTION MATERIALS OF SHIP","authors":"E. Y. Sari, P. Nasution, Fajri Ramdhan","doi":"10.20956/JIKS.V5I1.7038","DOIUrl":null,"url":null,"abstract":"Parameters for measuring the physical properties on this research are divided into three elements, including measurement of weight, water absorption, and density. This research was conducted from January to March 2018 to determine the physical properties of wood powder composites and bagasse. The manufacturing and testing process refers to the ASTM and JIS standards. Weight and density testing refer to the ASTM D 792 standard while the water absorption test refers to the JIS A5908 standard. The results showed that the density of wood powder was 0.4175 gr / cm3, and the bagasse was 0.3125 gr / cm3. Then, fiber absorption in units of volume to water and resin were 16.88% and 13.75% respectively. The results showed that the largest water absorption was found in composite wood powder 60% and bagasse 40%, which was 13.47%, and for the highest density values found in wood powder composites as much as 80% or 1,078.29 kg / m3","PeriodicalId":55804,"journal":{"name":"Jurnal Ilmu Kelautan Spermonde","volume":" ","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2019-07-15","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"2","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Jurnal Ilmu Kelautan Spermonde","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.20956/JIKS.V5I1.7038","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 2
Abstract
Parameters for measuring the physical properties on this research are divided into three elements, including measurement of weight, water absorption, and density. This research was conducted from January to March 2018 to determine the physical properties of wood powder composites and bagasse. The manufacturing and testing process refers to the ASTM and JIS standards. Weight and density testing refer to the ASTM D 792 standard while the water absorption test refers to the JIS A5908 standard. The results showed that the density of wood powder was 0.4175 gr / cm3, and the bagasse was 0.3125 gr / cm3. Then, fiber absorption in units of volume to water and resin were 16.88% and 13.75% respectively. The results showed that the largest water absorption was found in composite wood powder 60% and bagasse 40%, which was 13.47%, and for the highest density values found in wood powder composites as much as 80% or 1,078.29 kg / m3
本研究中测量物性的参数分为三个要素，分别是测量重量、吸水率和密度。本研究于2018年1月至3月进行，以确定木粉复合材料和甘蔗渣的物理性能。制造和测试过程参照ASTM和JIS标准。重量和密度试验参照ASTM D 792标准，吸水试验参照JIS A5908标准。结果表明，木粉的密度为0.4175 gr / cm3，甘蔗渣的密度为0.3125 gr / cm3。单位体积纤维对水和树脂的吸收率分别为16.88%和13.75%。结果表明，木粉复合材料的吸水率最高，分别为60%和40%，分别为13.47%;木粉复合材料的密度最高，分别为80%和1,078.29 kg / m3
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们