{"title":"Long‐Length YBCO Coated Stainless Steel Tapes with High Critical Currents","authors":"A. Usoskin, A. Rutt, J. Knoke, R. Dietrich","doi":"10.1063/1.2192414","DOIUrl":null,"url":null,"abstract":"Progress in manufacturing 40m long YBCO coated stainless steel tapes by ion beam assisted deposition and by high‐rate pulsed laser deposition is reported. A critical current of 84.5A (77K, self field) was observed for end‐to‐end measurements of the 40m long tape based on a 1.05μm thick and 3.6mm wide YBCO film. This implies that a critical current of 235A per cm‐width is achieved by just a 1 μm thick YBCO layer. Analysis of the influence of local defects onto the integral U(I) curves allowed to formulate a general criterion for the homogeneity in terms of reduced number of tape parameters.A deterioration of tapes induced by mechanical torsion starts at a very high deformation degree: irreversibility threshold corresponds to 3000 angular degrees per meter for 4mm wide coated tape loaded with a 40N tensile axial force.","PeriodicalId":80359,"journal":{"name":"Advances in cryogenic engineering","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2006-04-21","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://sci-hub-pdf.com/10.1063/1.2192414","citationCount":"10","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Advances in cryogenic engineering","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1063/1.2192414","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 10
Abstract
Progress in manufacturing 40m long YBCO coated stainless steel tapes by ion beam assisted deposition and by high‐rate pulsed laser deposition is reported. A critical current of 84.5A (77K, self field) was observed for end‐to‐end measurements of the 40m long tape based on a 1.05μm thick and 3.6mm wide YBCO film. This implies that a critical current of 235A per cm‐width is achieved by just a 1 μm thick YBCO layer. Analysis of the influence of local defects onto the integral U(I) curves allowed to formulate a general criterion for the homogeneity in terms of reduced number of tape parameters.A deterioration of tapes induced by mechanical torsion starts at a very high deformation degree: irreversibility threshold corresponds to 3000 angular degrees per meter for 4mm wide coated tape loaded with a 40N tensile axial force.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们