{"title":"Fe<sub>3</sub>O<sub>4</sub> and Fe Nanoparticles by Chemical Reduction of Fe(acac)<sub>3</sub> by Ascorbic Acid: Role of Water","authors":"Ajinkya Nene, M. Takahashi, P. Somani","doi":"10.4236/WJNSE.2016.61002","DOIUrl":null,"url":null,"abstract":"Nanoparticles of Fe3O4 and Fe are chemically synthesized by reduction of Fe(acac)3 using ascorbic acid in controlled condition. It was observed that addition of water during the chemical synthesis process yields Fe3O4 nanoparticles, whereas if the reaction is carried out in absence of water yields Fe nanoparticles—which get oxidized upon exposure to air atmosphere. Fe3O4 (15 ± 5 nm) and Fe/iron oxide nanoparticles (7 ± 1 nm) were successfully synthesized in the comparative study reported herewith. Mechanism for formation/synthesis of Fe3O4 and Fe/iron oxide nanoparticles is proposed herewith in which added water acts as an oxygen supplier. Physico-chemical characterization done by SEM, TEM, EDAX, and XPS supports the proposed mechanism.","PeriodicalId":66816,"journal":{"name":"纳米科学与工程(英文)","volume":"06 1","pages":"20-28"},"PeriodicalIF":0.0000,"publicationDate":"2016-01-15","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"25","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"纳米科学与工程(英文)","FirstCategoryId":"1089","ListUrlMain":"https://doi.org/10.4236/WJNSE.2016.61002","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 25
Abstract
Nanoparticles of Fe3O4 and Fe are chemically synthesized by reduction of Fe(acac)3 using ascorbic acid in controlled condition. It was observed that addition of water during the chemical synthesis process yields Fe3O4 nanoparticles, whereas if the reaction is carried out in absence of water yields Fe nanoparticles—which get oxidized upon exposure to air atmosphere. Fe3O4 (15 ± 5 nm) and Fe/iron oxide nanoparticles (7 ± 1 nm) were successfully synthesized in the comparative study reported herewith. Mechanism for formation/synthesis of Fe3O4 and Fe/iron oxide nanoparticles is proposed herewith in which added water acts as an oxygen supplier. Physico-chemical characterization done by SEM, TEM, EDAX, and XPS supports the proposed mechanism.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们