{"title":"Effect of In on Fe phase morphology and properties of Cu-Fe alloy","authors":"Dawei Yuan, Zhenxia Liu, Cheng-jun Guo, Hao Zeng, Jianbo Zhang, Mingmao Li, B. Peng, Bin Yang","doi":"10.1080/02670836.2023.2246773","DOIUrl":null,"url":null,"abstract":"ABSTRACT In this paper, Cu-6.2Fe-xIn (x = 0, 0.2, 0.4) alloy was prepared by melting casting and mechanical heat treatment. The Fe phase morphology of Cu-6.2Fe-xIn alloy was observed by SEM, EBSD and TEM. The results show that the addition of In element refines the primary Fe phase and optimises its distribution. After large plastic deformation, the Fe phase was fibrillated and the addition of In refines the Fe fibre and increases its density. The strength of Cu-6.2Fe-0.4In alloy with strain of 7 were 901 MPa, which was 201 MPa higher than that of Cu-6.2Fe alloy. The refining effect of In on the primary Fe phase was the main reason for the significant improvement of the strength of Cu-Fe-In alloy.","PeriodicalId":18232,"journal":{"name":"Materials Science and Technology","volume":"8 1","pages":""},"PeriodicalIF":1.7000,"publicationDate":"2023-08-20","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Science and Technology","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1080/02670836.2023.2246773","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0
Abstract
ABSTRACT In this paper, Cu-6.2Fe-xIn (x = 0, 0.2, 0.4) alloy was prepared by melting casting and mechanical heat treatment. The Fe phase morphology of Cu-6.2Fe-xIn alloy was observed by SEM, EBSD and TEM. The results show that the addition of In element refines the primary Fe phase and optimises its distribution. After large plastic deformation, the Fe phase was fibrillated and the addition of In refines the Fe fibre and increases its density. The strength of Cu-6.2Fe-0.4In alloy with strain of 7 were 901 MPa, which was 201 MPa higher than that of Cu-6.2Fe alloy. The refining effect of In on the primary Fe phase was the main reason for the significant improvement of the strength of Cu-Fe-In alloy.
期刊介绍：
《Materials Science and Technology》（MST） is an international forum for the publication of refereed contributions covering fundamental and technological aspects of materials science and engineering.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们