{"title":"Microstructure and mechanical properties of 20Si2CrNi3MoV steel treated by HDQP process","authors":"Chuan-feng Meng , Lei Zhang , Cun-yu Wang , Yu-jie Zhang , Ying-hui Wei , Yi-de Wang , Wen-quan Cao","doi":"10.1016/S1006-706X(17)30165-6","DOIUrl":null,"url":null,"abstract":"<div><p>A combined process of hot-deformation plus two-step quenching and partitioning (HDQP) treatment was applied to a low-carbon 20Si2CrNi3MoV steel, and transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD), Vickers hardness and tension test were used to characterize the microstructure and mechanical properties. More stable retained austenite due to fine microstructures and typical curved micromorphology is obtained, and the newly-treated steel obtains more retained austenite because of the effect of hot deformation. The retained austenite fraction increases and then decreases with the increasing quenching temperature from 200 to 350 °C. The maximum retained austenite fraction (18. 3%) and elongation (15%) are obtained to enhance the ductility.</p></div>","PeriodicalId":64470,"journal":{"name":"Journal of Iron and Steel Research(International)","volume":"24 11","pages":"Pages 1137-1142"},"PeriodicalIF":3.1000,"publicationDate":"2017-11-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://sci-hub-pdf.com/10.1016/S1006-706X(17)30165-6","citationCount":"1","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Iron and Steel Research(International)","FirstCategoryId":"1087","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S1006706X17301656","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"METALLURGY & METALLURGICAL ENGINEERING","Score":null,"Total":0}
引用次数: 1
Abstract
A combined process of hot-deformation plus two-step quenching and partitioning (HDQP) treatment was applied to a low-carbon 20Si2CrNi3MoV steel, and transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD), Vickers hardness and tension test were used to characterize the microstructure and mechanical properties. More stable retained austenite due to fine microstructures and typical curved micromorphology is obtained, and the newly-treated steel obtains more retained austenite because of the effect of hot deformation. The retained austenite fraction increases and then decreases with the increasing quenching temperature from 200 to 350 °C. The maximum retained austenite fraction (18. 3%) and elongation (15%) are obtained to enhance the ductility.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们