Evolution of microstructure, mechanical and magnetic properties of electrodeposited 50% Ni-Fe alloy foil after thermal treatment

Abstract

In order to expand the application of the electrodeposited Ni-Fe alloy foil, their mechanical and magnetic properties were studied after heat treatment. The development of grain growth during annealing was in-situ online investigated using a heating stage microscope, and the texture was analyzed via X-ray diffraction (XRD) and electron back-scattered diffraction (EBSD). The results indicated that abnormal grain growth usually occurred during annealing at 1000–1050 °C. The {111} oriented grains preferentially grew as the annealing temperature and holding time increased. The plasticities of the electrodeposited Ni-Fe alloy foils after heat treatment were better than those of the original samples. The excellent ductility was obtained without a loss in magnetic properties after annealing at 1100 °C for 6 h.