{"title":"INVESTIGATION OF PULSE FREQUENCY ON FUSION ZONE CHARACTERISTICS OF GTA WELDED AZ31B MAGNESIUM ALLOY JOINTS","authors":"Subravel V","doi":"10.37255/jme.v15i2pp50-53","DOIUrl":null,"url":null,"abstract":"In this investigation an attempt has been made to study the effect of welding on fusion\ncharacteristics of pulsed current gas tungsten arc welded AZ31B magnesium alloy joints. Five joints were fabricated using different levels of welding speed (105 mm/min –145 mm/min). From this investigation, it is found that the joints fabricated using a welding speed of 135 mm/min yielded superior tensile properties compared to other joints. The formation of finer grains and higher hardness in fusion zone and uniformly distributed precipitates are the main reasons for the higher tensile properties of these joints","PeriodicalId":38895,"journal":{"name":"Academic Journal of Manufacturing Engineering","volume":"112 1","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2020-06-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Academic Journal of Manufacturing Engineering","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.37255/jme.v15i2pp50-53","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"Engineering","Score":null,"Total":0}
引用次数: 0
Abstract
In this investigation an attempt has been made to study the effect of welding on fusion
characteristics of pulsed current gas tungsten arc welded AZ31B magnesium alloy joints. Five joints were fabricated using different levels of welding speed (105 mm/min –145 mm/min). From this investigation, it is found that the joints fabricated using a welding speed of 135 mm/min yielded superior tensile properties compared to other joints. The formation of finer grains and higher hardness in fusion zone and uniformly distributed precipitates are the main reasons for the higher tensile properties of these joints
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们