Chenglin Liu , Gu Jianhua , Li Yuanguang , Zhong Juhua , Zhang Zhaokui
{"title":"Studies on fabricating α-Fe2O3 ultrafine particles by LB film technology","authors":"Chenglin Liu , Gu Jianhua , Li Yuanguang , Zhong Juhua , Zhang Zhaokui","doi":"10.1016/S0968-5677(98)00075-3","DOIUrl":null,"url":null,"abstract":"<div><p>The <em>α</em>-Fe<sub>2</sub>O<sub>3</sub> ultrafine particles were dispersed in the solutions of stearic acid/<em>n</em>-hexane/chloroform by the ultrasonic method, and fabricated by the Langmuir–Blodgett film technology. <em>α</em>-Fe<sub>2</sub>O<sub>3</sub> ultrafine particles/stearic acid composite LB films were characteried by <em>π</em>–A curve, UV-visible absorption spectrum, IR spectrum, small angle X-ray diffraction, TEM and electron diffraction. The results showed the following: the <em>α</em>Fe<sub>2</sub>O<sub>3</sub> ultrafine particles were uniformly dispersed in organic solvents; the film-forming characterization of the <em>α</em>-Fe<sub>2</sub>O<sub>3</sub> ultrafine particles/stearic acid monolayer was fine, the <em>α</em>-Fe<sub>2</sub>O<sub>3</sub> ultrafine particles in the composite film had a small orientation; the <em>α</em>-Fe<sub>2</sub>O<sub>3</sub> ultrafine particles/stearic acid composite film had a lamellar structure.</p></div>","PeriodicalId":22050,"journal":{"name":"Supramolecular Science","volume":"5 5","pages":"Pages 565-567"},"PeriodicalIF":0.0000,"publicationDate":"1998-10-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://sci-hub-pdf.com/10.1016/S0968-5677(98)00075-3","citationCount":"2","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Supramolecular Science","FirstCategoryId":"1085","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0968567798000753","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 2
Abstract
The α-Fe2O3 ultrafine particles were dispersed in the solutions of stearic acid/n-hexane/chloroform by the ultrasonic method, and fabricated by the Langmuir–Blodgett film technology. α-Fe2O3 ultrafine particles/stearic acid composite LB films were characteried by π–A curve, UV-visible absorption spectrum, IR spectrum, small angle X-ray diffraction, TEM and electron diffraction. The results showed the following: the αFe2O3 ultrafine particles were uniformly dispersed in organic solvents; the film-forming characterization of the α-Fe2O3 ultrafine particles/stearic acid monolayer was fine, the α-Fe2O3 ultrafine particles in the composite film had a small orientation; the α-Fe2O3 ultrafine particles/stearic acid composite film had a lamellar structure.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们