{"title":"Influence of Gadolinium Addition on Mechanical and Corrosion Properties of 2205 Duplex Stainless Steel","authors":"Jae-Han Lim, Ji-Ho Ahn, B. Moon, Young-Jig Kim","doi":"10.7777/JKFS.2015.35.6.163","DOIUrl":null,"url":null,"abstract":"This study reports the influence of gadolinium (Gd) addition on mechanical and corrosion properties of 2205 duplex stainless steel. In all alloys produced, regardless of the initial Gd content, Gd-based inclusions were well distributed in the duplex stainless steel matrix. As the Gd content increased from 0 wt% to 0.19 wt%, the ultimate tensile strength and hardness of the alloy increased from 630 MPa to 977 MPa and from 57 to 61, respectively, while elastic modulus, tensile elongation and impact energy of the alloy decreased. The critical crevice temperatures of Alloy1, Alloy2 and Alloy3 were , and , respectively.","PeriodicalId":16318,"journal":{"name":"Journal of Korea Foundry Society","volume":"206 1","pages":"163-169"},"PeriodicalIF":0.0000,"publicationDate":"2015-12-31","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Korea Foundry Society","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.7777/JKFS.2015.35.6.163","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
This study reports the influence of gadolinium (Gd) addition on mechanical and corrosion properties of 2205 duplex stainless steel. In all alloys produced, regardless of the initial Gd content, Gd-based inclusions were well distributed in the duplex stainless steel matrix. As the Gd content increased from 0 wt% to 0.19 wt%, the ultimate tensile strength and hardness of the alloy increased from 630 MPa to 977 MPa and from 57 to 61, respectively, while elastic modulus, tensile elongation and impact energy of the alloy decreased. The critical crevice temperatures of Alloy1, Alloy2 and Alloy3 were , and , respectively.