{"title":"Al/Fe 2 O 3 /PTFE反应材料制备及性能","authors":"陶忠明, 方向, 李裕春, 冯彬, 王怀玺","doi":"10.11943/J.ISSN.1006-9941.2016.08.010","DOIUrl":null,"url":null,"abstract":"采用模压烧结法制备Al/Fe2O3/聚四氟乙烯(PTFE)反应材料。通过万能实验机、落锤仪以及高速摄影仪对不同配比及烧结温度下成型Al/Fe2O3/PTFE反应材料的准静态压缩力学特性及撞击感度进行了对比实验, 对其发火性能进行了分析。结果显示, 330 ℃烧结、PTFE含量为60%和70%的试件强度最高, 最大真实应力达到46 MPa。350 ℃烧结、PTFE含量为40%的试件撞击感度最高, 其特性落高H50为95 cm。Al/Fe2O3/ PTFE反应材料在受撞击发火的条件下会出现高温金属熔渣喷射现象。","PeriodicalId":35753,"journal":{"name":"Hanneng Cailiao/Chinese Journal of Energetic Materials","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2016-08-25","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Hanneng Cailiao/Chinese Journal of Energetic Materials","FirstCategoryId":"1087","ListUrlMain":"https://doi.org/10.11943/J.ISSN.1006-9941.2016.08.010","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"Engineering","Score":null,"Total":0}
引用次数: 0
引用
批量引用
Al/Fe 2 O 3 /PTFE反应材料制备及性能
采用模压烧结法制备Al/Fe2O3/聚四氟乙烯(PTFE)反应材料。通过万能实验机、落锤仪以及高速摄影仪对不同配比及烧结温度下成型Al/Fe2O3/PTFE反应材料的准静态压缩力学特性及撞击感度进行了对比实验, 对其发火性能进行了分析。结果显示, 330 ℃烧结、PTFE含量为60%和70%的试件强度最高, 最大真实应力达到46 MPa。350 ℃烧结、PTFE含量为40%的试件撞击感度最高, 其特性落高H50为95 cm。Al/Fe2O3/ PTFE反应材料在受撞击发火的条件下会出现高温金属熔渣喷射现象。
本文章由计算机程序翻译，如有差异，请以英文原文为准。
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们