Magdalena Rajczakowska, M. Szeląg, K. Habermehl-Cwirzen, H. Hedlund, A. Ćwirzeń
{"title":"Is Cement Paste Modified with Carbon Nanomaterials Capable of Self-Repair after a Fire?","authors":"Magdalena Rajczakowska, M. Szeląg, K. Habermehl-Cwirzen, H. Hedlund, A. Ćwirzeń","doi":"10.2478/ncr-2022-0017","DOIUrl":null,"url":null,"abstract":"Abstract This manuscript presents preliminary results on the cement paste potential, with and without carbon nanomaterials, to heal high-temperature cracks. Cement paste beams were subjected to thermal loading of 200°C and 400°C after 28 days of water curing. High temperature caused the formation of microcrack networks on the specimen’s surface. Self-healing was achieved by exposing the cracked samples to cyclic water immersion. The efficiency of the process was evaluated based on the crack closure and mechanical properties recovery after 24 days. The results indicated a distinct dependence of the healing on the loading temperature. Carbon nanotubes had a positive effect on self-repair efficiency.","PeriodicalId":42762,"journal":{"name":"Nordic Concrete Research","volume":null,"pages":null},"PeriodicalIF":0.7000,"publicationDate":"2022-12-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"1","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Nordic Concrete Research","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.2478/ncr-2022-0017","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"CONSTRUCTION & BUILDING TECHNOLOGY","Score":null,"Total":0}
引用次数: 1
Abstract
Abstract This manuscript presents preliminary results on the cement paste potential, with and without carbon nanomaterials, to heal high-temperature cracks. Cement paste beams were subjected to thermal loading of 200°C and 400°C after 28 days of water curing. High temperature caused the formation of microcrack networks on the specimen’s surface. Self-healing was achieved by exposing the cracked samples to cyclic water immersion. The efficiency of the process was evaluated based on the crack closure and mechanical properties recovery after 24 days. The results indicated a distinct dependence of the healing on the loading temperature. Carbon nanotubes had a positive effect on self-repair efficiency.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们