Liu Hong-bo, Lin Feng, Xiao Wang-dong, X. Ling, Zhang Wu-ying
{"title":"Surface Properties of UV-Heat Cured Films of Organosilicon Modified Epoxy Monoacrylates","authors":"Liu Hong-bo, Lin Feng, Xiao Wang-dong, X. Ling, Zhang Wu-ying","doi":"10.7517/J.ISSN.1674-0475.2013.02.005","DOIUrl":null,"url":null,"abstract":"A series of UV-heat hybrid curable compositions were prepared by using organosilicon modified epoxy monoacrylates(OMEMA) as resins.The change of absorption peaks of double bond and epoxy group were identified by FTIR spectra during UV-heat curing process.The influence of different kinds and content of active diluents on the gel content,water absorption and water contact angle of UV-heat cured films were investigated.Mass content of Si in surface of UV-heat cured films was tested by the energy dispersive spectrometer(EDS).The gel contents of UV cured films were lower than 86.5%,and the gel contents of UV-heat cured films were about 97%.Compared to the epoxy monoacrylates(EMA) compositions with same active diluents,the water contact angle of UV-heat cured films of OMEMA system was increased from 62.53 to 99.27.The data of EDS testing proved that the Si content of air side of UV-heat cured films was higher than glass side.","PeriodicalId":13253,"journal":{"name":"","volume":"17 1","pages":"125"},"PeriodicalIF":0.0,"publicationDate":"2013-03-15","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"","FirstCategoryId":"1087","ListUrlMain":"https://doi.org/10.7517/J.ISSN.1674-0475.2013.02.005","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
A series of UV-heat hybrid curable compositions were prepared by using organosilicon modified epoxy monoacrylates(OMEMA) as resins.The change of absorption peaks of double bond and epoxy group were identified by FTIR spectra during UV-heat curing process.The influence of different kinds and content of active diluents on the gel content,water absorption and water contact angle of UV-heat cured films were investigated.Mass content of Si in surface of UV-heat cured films was tested by the energy dispersive spectrometer(EDS).The gel contents of UV cured films were lower than 86.5%,and the gel contents of UV-heat cured films were about 97%.Compared to the epoxy monoacrylates(EMA) compositions with same active diluents,the water contact angle of UV-heat cured films of OMEMA system was increased from 62.53 to 99.27.The data of EDS testing proved that the Si content of air side of UV-heat cured films was higher than glass side.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们